与探讨延长高炉炉底炉缸寿命的方法.pdfVIP

探讨延长高炉炉底炉缸寿命的方法 ·1 · 探讨延长高炉炉底炉缸寿命的方法 陈兴家 徐吉林 战 奇 （鞍钢集团工程技术有限公司，鞍山 114021 ） 摘 要 在冷却能力不足的情况下，炉底炉缸衬体的各种间隙，因窜风窜水夹带着锌及其他碱金属，会加剧碳砖侵 蚀，特别是在铁口区域，情况会进一步恶化，严重者铁水侵入碳砖背部，极易酿成炉缸烧穿等重大事故。锌在高炉 内循环富集所带来的危害不容小视，广大炼铁同仁对锌危害虽有认识，却没有形成系统的方法和措施来应对。本文 力求采用系统分析从设计角度来找到解决问题的方法。 关键词 炉底炉缸 间隙 窜风窜水 锌危害 预防措施 长寿 Discussion on the Methods to Increase the Hearth Life the BF Hearth and Hearth Bottom Chen Xingjia Xu Jilin Zhan Qi (Ansteel Engineering Technology Co. , Ltd., Anshan, 114021) Abstract When BF cooling capacity is insufficient, and gaps existent between hearth furnace and hearth bottom, Zinc and alkali metal will increased erode carbon brick. What’s worse, hot metal will intrude into carbon brick back in taphole area. Under this circumstance, burning through accident is more likely to occur. Although the iron making colleagues are aware of the harm of Zn, haven’t form systemic methods and measures to deal with it. This paper aims at systematically analyzing these issues to find the solution. Key words BF hearth and hearth bottom, gaps, air leakage and water leakage, Zinc harm, preventive action, longevity 1 概述 近年来随着高炉大型化的快速发展，也带来了影响炉底炉缸寿命的新问题，例如，炉缸象脚状区域冷却 壁水温差增大，制约高炉强化生产，高炉被迫采取护炉措施，严重者在炉缸炉底区域出现热点，更有甚者投 产仅两年多就发生烧穿事故，给生产带来重大损失。鞍钢技术中心及鞍钢炼铁总厂曾对破损高炉做过检查， 初步证明高炉炉底炉缸部位冷却不足是主要原因，而 Zn 元素在炉底炉缸区域循环富集带来的危害更不容小 视。锌危害是近年才被发现的问题，但未能引起炼铁工作者的足够认识，或者说虽有认识，却没有形成系统 的方法和措施来应对。本文力求采用系统分析从设计角度来找到解决问题的方法。 2 高炉破损原因 3 鞍钢新 3 号高炉（V =3200m ）于2005 年 12 月28 日投产，2008 年 8 月25 日在没有先兆情况下发生炉 u 缸烧穿事故，造成巨大经济损失。为分析烧穿事故原因，由炼铁厂和技术中心相关人员组成调查小组，利用 抢修之机对高炉炉缸进行了一次破损检查。 陈兴家, 高级工程师。 ·2 · 第九届中国钢铁年会论文集 破损检查过程中发现，炉缸碳砖侵蚀程度极其不均匀，所有非铁