中厚板常化炉后快冷（NAC）技术装备.pdfVIP

中厚板常化炉后快冷（NAC）技术装备 李谋渭 张少军 边新孝 刘国勇 朱冬梅 王 琳 （北京科技大学，北京 100083 ） 摘 要 本文重点介绍中厚板常化炉后快冷（NAC ）的工艺特点、机型特点和关键技术，特别是冷却速率控制、钢 板均匀冷却控制和全板冷却目标温度控制技术，指出中厚板常化炉后快冷技术是一种行之有效的新技术。 关键词 常化炉 控冷 气雾冷却 管流 流量调控 The Technology and Equipment of the Accelerated Cooling After Plate Normalizing Furnace (NAC) Li Mouwei Zhang Shaojun Bian Xinxiao Liu Guoyong Zhu Dongmei Wang Lin （University of Science and Technology Beijing, Beijing, 100083 ） Abstract The paper introduce emphatically technology characteristics of the accelerated cooling after plate normalizing furnace(NAC) and model of a machine and key technologies, especially the cooling rate control, uniform cooling of steel plate cooling control and the whole cooling target temperature control technology, appointing the technology of the accelerated cooling after plate normalizing furnace is an effective new technology. Key words normalizing furnace, controlled cooling, air-water cooling, pipe flow, flow control 中厚板常化炉后快冷（NAC ）是由舞阳钢铁公司和北京科技大学联合研发的，是有我国独立知识产权 的技术装备。经过近8 年的实践，生产了100 万吨以上的优质钢板，取得了良好的效果，证明它是一种行之 有效的新技术： （1）可使钢板强度平均提高50MPa，冲击韧性提高30J 左右； （2 ）可以挽救轧线ACC 处理后性能不合格的钢板，提高钢板综合成材率； （3 ）热处理钢板性能合格率高，对一般钢种强度合格率可达96%~98%，对Q235 钢板强度合格率可达 99%； （4 ）可取消或降低某些常化钢种的微合金元素，降低生产成本； （5 ）可解决Cr-Mo 钢和高强度贝氏体钢在常规空冷下无法达到的相变要求； （6 ）通过多年实践，已对低合金钢、高屈服强度钢、高强度船板、非临氢类Cr-Mo 钢、临氢类 Cr-Mo 钢、模具钢等钢种产生良好的工艺效果，这种效果将随新材料的开发而不断加大。 1 工艺特点 常化炉后快冷与常规常化炉后空冷不同，它是以高于一般空冷的冷却速度对钢板进行冷却控制，以提高 材料的力学性能和改善其组织结构。 2 机型特点 采用气雾冷却和高密集管流组合结构，可分强中弱进行冷却强度控制，利用高位水箱节能稳压，通过流 量调控装置均匀流量分配。它是在太钢多功能淬火机专利技术基础上发展起来的机型，如图1 所示。 中厚板常化炉后快冷（NAC ）技术装备 8-379 3 关键技术 3.1 冷却速率控制技术 根据快冷工艺要求和快冷钢种的多样化，要求常化炉后快冷 装置要具备较宽的冷却速率控制范围，从传热学角度来说，即要 求对钢板有较宽的换热系数。气雾冷却控冷技术和高密集管流控 冷技术的有机组合，为常化炉后快冷提供了较宽的控冷手段。图 [1]