连退产品氧化色原因分析及对策 罗 诚 （攀钢冷轧厂，攀枝花 617023 ） 摘 要 本文主要就连退产品氧化色产生的原因，从退火炉设备、烧嘴工艺参数、燃烧介质及炉内气氛的控制等方 面进行深入研究分析，找出了其具体原因，并阐述了氧化色缺陷对连退产品质量的影响，根据现场实际情况制定相 应的措施来消除连退产品的氧化色缺陷，从而提高连退产品的质量，使得连退产品的市场竞争力得到很大程度的提 高，对其产品的市场形象具有极其重要的意义。1 关键词 产品质量 氧化色 炉内气氛 原因分析对策 TheReasonAnalysisandCountermeasureonSeriesAnneal StripSteelBeingOxidation Luo Cheng （Cold Strip Mill of Panzhihua Iron Steel Co., Ltd., Panzhihua, 617023 ） Abstract In this paper, the color on annealing causes oxidation products from the furnace equipment, process parameters burner, burning furnace atmosphere control the media and other aspects of in-depth research and analysis, to identify its specific causes, and describes the oxidation color defects annealing effect on product quality, according to the situation on the development of appropriate measures to eliminate the oxidation products annealing color defects, thereby enhancing the quality of the product annealing, annealing makes the product competitive in the market has been largely improved, the the image of its products in the market is extremely important. Key words production quality , oxidation, atmosphere of anneal furnace, reason analysis, countermeasure 1 引言 某厂连续退火生产线是利用原来的镀锌生产线改造而来，同样采用改良森吉米尔法。其中连续退火炉主 要设置了废气预热段RWP 、无氧化加热段NOF 、辐射管加热段RTH 、缓冷段SC、喷冷段GJS、低温保持 段LTH 以及TDS 段（原热张辊处），其中NOF 、RTH 又各分为3 个小段（1Z、2Z、3Z ），GJS 又分为两个 小段（1Z、2Z ）。退火炉在改造后，带钢从LTH 段尾部的新增热张辊处进入立式炉。立式炉分为过时效段OAS, 最终冷却段FCS 。退火炉的炉内气氛稳定对退火炉的安全运行提供了必要的条件。为了保证退火炉的炉内气 氛稳定，在退火炉的尾部TDS 段引入氮氢混合站的氮氢保护气体及在立式炉新增了一套氮氢混合站将氮氢 保护气体引入立式炉内(N2H2 以最大5%的H2 含量混合以充分保护带钢) 。在废气预热段RWP 采用烟气预热 将带钢表面的轧制油烧掉并预热带钢，在无氧化加热段NOF 采用明火烧嘴快速加热带钢（由3 段烧嘴分别 控制），与此同时在带钢表面会形成一层很薄的氧化膜，这层氧化膜将通过通入炉内的氮氢保护气体消除。 若在NOF 段出现自由氧的话（自由氧存在极强的氧化性），将造成这层氧化膜过厚，不能通过氮氢保护气体 1罗诚，男，技术员，从事镀锌设备维护管理工作。电话