SS400钢激光焊接参数设定的分析 肖公辉 柴志鹏 （河北钢铁集团邯钢公司冷轧厂，邯郸 056015 ） 摘 要 本文从实践与理论相结合的角度，对邯钢冷轧厂SS400 品种钢实际焊接生产中存在的焊缝质量合格率低， 容易造成断带事故的问题，从激光焊机原理与原材料成分等方面进行了分析，得出SS400 钢在激光焊接过程中对焊 缝质量影响的相关因素，并对其进行了具体的优化，设定合适焊接参数标准，使其达到最佳状态。 关键词 激光 深熔焊 焊缝质量 SS400 钢 TheAnalysisofSS400SteelLaserWeldingParameters Xiao Gonghui Chai Zhipeng （The Hangang Cold Rolling Plant of Hebei Iron and Steel Co.,Ltd., Handan, 056015 ） Abstract This combination of practice and theory from the perspective of the Handan Iron and Steel Cold Rolling Mill Steel SS400 species exist in the actual welding low pass weld quality, easy to break with the accident causing the problem, from the principle of laser welding machine and raw material composition etc. analyzed, obtained SS400 steel in laser welding process, weld quality on the impact of relevant factors and the specific optimization was carried out, to set appropriate standards of welding parameters to reach the best. Key words laser, deep welding, welding seam quality, SS400 Steel 1 引言 激光焊机作为一种新型焊接设备，越来越广地被应用到各种领域。在邯钢酸洗冷连轧生产机组中， 钢卷间的连接就是由激光焊机完成的，它起到了一个承前启后的作用，保证了酸轧线生产的连续性。 通过生产实践对 SS400 钢焊接设定参数的跟踪统计，因其参数与普通钢有所区别，所以其焊接参数的 正确设定，直接关系到焊缝质量的好坏，因此对SS400 钢焊接参数标准的设定显得尤为重量，必须加 以分析与优化。 2 激光焊接原理 激光对金属材料的加工主要是基于光热效应的热加工，其前提是激光为被加工材料所吸收并转化为热。 在不同功率密度的激光束的照射下，材料表面区域将发生各种不同的变化，这些变化包括表面温度升高、熔 化、汽化、形成小孔以及产生光束等离子体等。当激光功率密度达到一定的高度，激光不仅使得金属熔化， 6 2 而且使熔化的金属产生汽化。这个功率密度应高于一临界值，一般为10 W/cm 。如图1 所示为激光功率及 功率密度与焊接深度的关系。可以看出，在临界功率密度Ic 附近，激光焊接深度突然加深，就转化为深熔 焊接。 8-642 第八届（2011 ）中国钢铁年会论文集 图1 激光功率密度与焊接 高功率CO2 激光焊机是先将二氧化碳（CO2 ）、氦气（He ）、氮气（ N2 ）三种气体混合后，通过高频 电压激励转化成高功率密度的激光束照射到被焊工件表面，短时间内能量被充分吸收，致使局部熔化，同时 并采用氦气（He ）作为保护气体，防