不锈钢铁水包喷吹脱磷工艺水模型实验研究.pdfVIP

第十五届全国炼钢学术会议文集 不锈钢铁水包喷吹脱磷工艺水模型实验研究 罗顶飞 徐安军 田乃媛 （北京科技大学冶金与生态工程学院，北京 100083） 摘 要： 通过铁水包喷吹脱磷工艺水模拟实验，对不同工艺条件下熔池混匀时间及液面喷溅进行实测，研 究了脱磷剂加入速度、铁水装入量、氧枪枪位、喷粉枪枪位、氧气流量、氮气流量对熔池流场的影响规律， 并结合工业试验，针对宝钢不锈钢分公司的实际生产工艺，得出了最佳的铁水包喷吹脱磷工艺参数范围， 指导现场操作。 关键词：铁水脱磷，水模型，混匀时间 Stainless Steel Hot Metal Package Dephosphorization of Water Model Experimental Study LUO Dingfei XU Anjun TIAN Naiyuan (School of Metallurgical and Ecological Engineering,USTB 100083) ABSTRACT ：Dephosphorization packets of hot metal through the injection of water simulation experiments, under the conditions of the different processes fused bath mixing time and measured a surface splash to Measure 。 Research dephosphorizing speed, load of molten iron, oxygen gun site, nitrogen gun site, the flow of oxygen, the flow of nitrogen, nitrogen traffic flow on the pool of the impact, combined with industrial testing, Baosteel Stainless Steel Branch for the actual production process, that the best package of hot metal injection dephosphorization process parameters, Guiding operation at the scene. KEY WORDS: Dephosphorization ，Water Model ，Mixing Time 1 概述 近年来，随着用户对钢的质量要求不断提高。例如，对于低温用钢、海洋用钢、抗氢致断裂纹钢和部 分厚板用钢等，除了要求极低的硫含量以外，也要求钢中的磷含量在 0.01～0.05 ％。为了生产低磷、超低 磷钢种，国内外各大钢铁公司相继开发了铁水包或混铁车铁水三脱技术(脱硅、脱硫及脱磷) ，并均已投入 了工业化生产。 对采用高炉铁水为部分原料生产不锈钢而言,采用铁水脱磷技术是必要的，脱磷后铁水中w [P] ≤0. 010 %～0. 015 % 。冶炼不锈钢的铁水脱磷一般采用铁水包脱磷方法[1~3] 。 宝钢不锈钢公司根据不锈钢生产工艺及产品大纲要求，采用了铁水包喷吹法进行铁水脱磷预处理工 艺。脱磷剂消耗平均为较高，经过脱磷剂的改进工作，脱磷剂消耗下降到平均 35.5kg/t，但和世界先进水 平相比，还存在一定的差距，还有潜力可挖。 2 实验原理 铁水包内铁液的流动，可视为黏性不可压缩流动。因此，系统只要满足几何相似和动力学相似就可以 满足模型和原型的相似[4～6] 2.1 几何相似 根据相似原理建立物理模型，用有机玻璃代替耐火材