大流动性水泥净浆与砂浆流变参数的测定方法.pdfVIP

第 4 卷第 2 期 建 　筑 　材 　料 　学 　报 Vol. 4 , No. 2 2001 年 6 月 JOURNAL OF BU ILDIN G MA TERIAL S 　 J un. ,2001 　　文章编号 (2001) 大流动性水泥净浆与砂浆流变参数的测定方法 杨　静 , 　王宏宇 (清华大学 土木工程系 ,北京 100084) 摘要 : 设计了 U 型流动仪以测定大流动性水泥净浆与砂浆的流变学特性 ,并通过改变水 灰比、减水剂掺量、骨料与浆体的质量比等参数 ,检验了该流动仪的有效性、敏感性及其适 用范围. 结果表明 ,U 型流动仪适用于测定大流动性水泥净浆与砂浆的流变参数. 关键词 : U 型流动仪 ; 流动时间 ; 流变学特性 中图分类号: TQ172. 1 + 6 　　　文献标识码 :A Ne w Method to Evaluate Rheological Behavior of High Fluidity Cement Paste and Mortar YA N G Jin g , 　W A N G Hon gyu (Department of Civil Engineering , Tsinghua University , Beijin g 100084 , China) Abstract : A new Ut ype flowmeter was used to evaluate the rheological behavior of cement paste and mortar with high fluidity , and the experiment was mainly carried on the flow time of the mortar. By changing watercement ratio , the content of superplasticizer and the mass ratio of the aggregate to the paste , the validity , sensitivit y and scope of this method were tested. A new method to evaluate rheo logical behavior of high fluidity cement paste and mortar is proposed in this paper. Key words : Ut ype flowmeter ; flow time ; rheological behavior 　　混凝土材料是利用“版筑技术”原理、由不定形的可塑性体经过浇注、捣实、抹平、养护等工序 ,并 等待其逐步硬化而形成的一种结构材料. 因此混凝土材料施工周期长,且性能受施工过程及其质量的 影响很大. 现代社会以混凝土为主要结构材料的工程建设量日益增大 ,并且要求施工速度快、易操作 和易控制质量、节省能耗 ,同时应尽量减少噪音、振动和粉尘之类的公害对环境所造成的不良影响. 在 这种背景下 ,从 20 世纪 80 年代开始 ,得益于高效减水剂、超塑化剂的研制成功 ,人们开发了大流动 性、免振自密实的混凝土 ,并且采用泵送浇注 ,这已成为当今混凝土施工方法的主要趋势. 与以往的混凝土材料相比 ,大流动性混凝土在原材料的种类、配比、内部结构及流变学特性等 方面差别很大. 它获得大流动性的手段是较低的水胶比及高效减水剂 ,而并非依靠加大用水量 , 因 此通常浆体的粘性较大. 另外 , 由于实际工程中对混凝土的强度、耐久性和结构密实性的要求越来 越高 ,这种混凝土的胶凝材料用量较大 ,除水泥之外 ,往往还掺入较多的超细粉矿物掺合料 , 同时砂 率较大 ,而粗骨料用量则较少 ,且其最大粒径也较小. 由于这些特点,大流动性混凝土富含水泥净浆 与砂浆