宝钢1450连铸生产技术的进步.docxVIP

2003 年第 3 期 宝 钢 技 术 15 宝钢 1450 连铸生产技术的进步 虞哲彪 (宝钢股份公司 炼钢厂 ,上海 200941) 摘要 :宝钢 1450 连铸投产 4 年多来生产持续稳定 ,缺陷率低 ,并创造了 27 000 炉无漏钢的 优异成绩 。文章从装备水平和工艺控制方面阐述了低缺陷无事故生产的技术 ,并介绍了改善 表面裂纹 、防止开浇漏钢以及开发宝钢独有的开浇管工艺等方面的经验 。 关键词 :无漏钢 ;表面裂纹 ;开浇管 中图分类号 : TF777 文献标识码 :B 文章编号 :1008 - 0716 (2003) 03 - 0015 - 04 Technical Progress in 1450 Continuous Casting at Baosteel YU Zhe2biao ( Baosteel Steelmaking Plant , Shanghai China ,200941) Abstract :Since its start2up operation ,Baosteel’s 1450mm continuous casting has had a stable pro2 duction and low defect rate. It has made 27 000 heats without breakout ,which is the best record in the world. The technology of CC slab with fewer defects and zero accident is introduced in this paper. The ex2 perience in preventing breakout in cast starting ,improving surface cracks ,and developing the unique pro2 cess of casting tubes is also introduced. Key Words :Breakout2free ;Surface crack ;Casting tube 1 前言 宝钢的 1450 连铸主机共二台 , 4 个浇铸流 , 设备主要是国内制造 ,部分采用“点菜式”方式引 进 。总体装备水平 、工艺控制和产品质量都是以 当时国际先进水平为目标 。 1450 连铸设计产量为 288 万 t/ 年 , 投产于 1998 年 4 月 ,同年 10 月达产 。4 年多来 ,1450 连 铸保持了持续稳定发展的良好态势 ,至 2002 年底 累计生产板坯 1 504. 03 万 t , 综合收得率达到 97. 03 % ,品种全面完成合同 ,主要经济技术指标 处于国际先进行列 ,创造了连续浇铸 27 000 炉无 漏钢的优异成绩 。 2 连铸机的装备水平 良 好的装备是高质量低事故的基础 。1450 虞哲彪 工程师 1947 年生 1983 年毕业于北京钢铁学院 现 从事连铸工艺研究工作 电话铸机的技术装备具有 20 世纪 90 年代中期的水 平 ,表现在提高连铸坯的质量和适应浇铸钢种广 泛性方面的有 : (1) 直弧形板坯连铸机 ,采用多点 弯曲和多点矫直 ,以减少铸坯的机械应力 ; (2) 采 用大容量的中间包并设有挡墙 ,振动为高频率小 振幅 ,二冷区导辊为小辊径多点支撑密辊排列 ; (3) 喷嘴采用气雾喷水 。一些措施还兼有提高生 产率和节能增效的现实意义 ,具体见表 1 、表 2 。 3 1450 连铸生产技术的进步 3. 1 冷却控制 3. 1. 1 一次冷却 结晶器是连铸的心脏 ,一次冷却技术是连铸 冷却技术的核心所在 。由于纯水水质稳定 ,传热 效果可控性强 ,故 1450 连铸采用纯水冷却 。 结晶器的铜板厚度为 55 mm。采用大厚度铜 板不仅使铜板使用的周期次数得到提高 ,也为实 现结晶器的缓冷控制提供了更大的物理空间 。 16 表 1 连铸机基本参数 Table 1 Basic parameters of CC machine 项 目 参 数 铸机类型 垂直弯曲 垂直高度 2 575 mm 浇注尺寸 厚度 230 mm 宽度 900～1 450 mm 长度 8～11 m、4～5 m 流数 2 弯曲点 7 矫直点 8 扇形段个数 18 冶金长度 ,m 37. 39 结晶器长度 ,mm 904 宝 钢 技 术 2003 年第 3 期 与对应浇铸钢种的裂纹敏感性相匹配是控制裂纹 的关键 。 (1) 结晶器冷却的计算 1450 连铸的结晶器冷却强度计算采用了一 次热传导计