添加剂在脱硫石膏中的应用 1 1 2 1 李英丁 ，张铬 ，郝艳 ，蔡挺 （1.汕头经济特区龙湖科技有限公司，汕头 515041； 2.西南科技大学先进建筑材料四川省重点实验室，绵阳621010） 要：测试了缓凝剂对脱硫石膏水化放热速率、绝干抗压强度的影响，同时测 试了有机硅防水剂对碱性石膏体系2h 吸水率、软化系数影响。结果表明缓凝 剂降低水化放热速率，推迟水化放热时间，有机硅防水剂显著降低脱硫石膏的 吸水率，同时大幅提高脱硫石膏的软化系数。 关键词：脱硫石膏；缓凝剂；防水剂 Application of additive in FGD gypsum 1 1 2 1 Yingding LI ， Ge ZHANG ， Yan HAO ，Ting CAI (1，Shantou S.E.Z. Longhu Sci. and Tech. Company Limited ，Shantou, 515041 ； 2, Southwest university of Science and Technology Key Laboratory for Advanced Building Materials of Sichuan Province,Mianyang,Sichuan,62 10 10) Abstract: The influence of the retarder on dry compressive strength and exothermic rate of hydration of FGD gypsum was tested, and the influence of silicone waterproofing agent on 2hours water absorption and softening coefficient of alkalescency gypsum. The analysis shows that retarder can reduce the exothermic rate of hydration, postpone exothermic time of hydration, silicone waterproofing agent reduced the water absorption and advanced the softening coefficient of FGD gypsum. Keywords: FGD gypsum ；Retarder ; Waterproofing agent 脱硫石膏是湿式石灰石－石膏法烟气脱硫工艺产生的工业副产品，对其进 行合理利用是各级政府大力倡导的项目。脱硫石膏可以大规模用于制品石膏砌 块，纸面石膏板、粉刷石膏等。脱硫石膏同天然石膏一样具有凝结时间短，耐 水性差特点，研究脱硫石膏的缓凝技术和防水技术情景广阔。 石膏硬化后具有吸湿性和吸水性，在潮湿的环境中，晶体间的粘结力减弱， 导致强度降低。处于水中的石膏晶体还会因为溶解而引起破坏，提高石膏的耐 水性是改善石膏性能，扩展石膏用途的重要途 ，添加有机硅防水剂是改善石 膏耐水性能的有效方法。 1.实验原材料的测试 脱硫石膏：标准稠度用水量58％，初凝时间17Min，终凝时间21Min，上 海产； 将脱硫石膏的衍射数据与PDF41-0224卡片对照,可以看出脱硫石膏的谱线 与卡片41-0224上数据相符,说明其主要的晶体为半水石膏。SEM照片 示半水 石膏晶体呈菱柱状，晶体结构相对完整，晶粒粗大。 表1 脱硫石膏化学成分 w (%) SiO CaO SO MgO Al O Fe O Other 2 3 2 3 2 3