首饰铸件浇注系统的优化设计.pdfVIP

学兔兔 Ju1．2009 铸 造 V0I．58 NO．7 FOUNDRY 首饰铸件浇注系统的优化设计 金英福 (延边大学工学院工业设计系，吉林延吉133002) 摘要：根据首饰铸件精密铸造工艺特点，对首饰铸件浇注系统中的浇12浇道进行分析。通过大量试验，发现浇口浇道 大小、连接角度的设计对首饰铸件质量有较大的影响；针对首饰铸件模型的不同结构提出了不同的浇口浇道的设计方 法，以消除铸件的各种缺陷，提高了铸件质量。 关键词：浇口；金属液；首饰铸件模型 中图分类号：TG242．1 文献标识码：B 文章编号：1001—4977(2009)07—0747—03 Optimal Design of Casting Inlet for Personal Ornaments JIN Ying-fu (Dept．of Industrial Design，College of Engineering，Yanbian University，Yanji 133002，Jilin，China) Abstract：According to the characteristics of precise casting of personal ornaments，the casting inlet of the gating system was analyzed and investigated．Through a lot of experiments，the diameter of the inlet and its connecting angle were found have great influence on quality of personal ornaments．Then the different designing method of inlet was put forward for ornaments with different structure，to eliminate all kinds of defects in the castings and provide reference for improvement of the ornaments quality． Key words：casting inlet；liquid metal；model of personal ornament 首饰铸件浇注系统的设计是首饰铸件精密铸造过 系统内液态金属的凝固趋于顺序凝固，浇注后的铸筒 程中的重要环节，除能控制液态金属的流速和方向外， 一 般在室温放置。经多次试验观察，铸筒内浇注后的 还具有分配金属液和补缩铸件的作用。在实际生产过 金属是从铸筒的外部向内部冷却，大部分的收缩都集 程中，常因对浇注系统的设计不合理而形成缩孔、缩 中在主浇道上。因此，浇口蜡尺寸应选择粗一些，使 松等铸造缺陷，使铸件的质量受到不良影响。为避免 金属凝固产生的收缩部分由浇口部分金属液补充。特 首饰铸件的铸造缺陷，笔者对首饰铸件浇口浇道的连 别是在浇注薄壁铸件时，若浇口蜡选择不合理，会降 接方式进行了分析和研究，旨在为获得良好的铸件浇 低金属液的流动性，不能及时补充铸型各部位金属液， 注效果提供参考。 加上金属凝固时的收缩，会导致铸件多孔。 1 浇注系统中浇口蜡的作用 2 浇口浇道的优化设计 首