钛脱氧低碳钢液凝固过程中氧化物的析出和长大.pdfVIP

维普资讯 学兔兔 Jun．2008 铸 造 VoI．57 NO．6 FOUNDRY ·553· 钛脱氧低碳钢液凝固过程中氧化物的析出和长大 尚德礼，吕春风，于广文 (鞍钢股份有限公司技术中心，辽宁鞍山114009) 摘要：通过试验，研究了低碳钢加钛脱氧后钢液中夹杂物的形态、组成、尺寸和类型，并研究了加钛前后钢的组织变 化。结果表明：加钛后，钢的组织明显细化，钛的脱氧产物可成为硫化锰夹杂的形核核心，也可以Ig]@~-A120。夹杂周 围，此类夹杂物呈细小弥散析出；这些细小的夹杂物可以在奥氏体晶粒内部诱导针状铁素体析出，从而产生细化组织 的效果。 关键词：氧化物冶金；夹杂物；晶内铁素体；Ti 中图分类号：TF703．5；TF762~．3 文献标识码：A 文章编号：1001—4977(2008)06-0553—04 Precipitation and Growth of Oxides During Solidification of Low Carbon SteeI Deoxidized with Ti SHANG De—li，LU Chun—feng，YU Guang—wen (TechnicaI Center，Angang SteeI Co．，Ltd．，Anshan 1 14009，Liaoning，China) Abstract：The morphology，chemicaI composition，size and type of inclusions in Iow carbon steeI deoxidized with Ti were investigated，and the microstructure evolvement before and after adding Ti was also analyzed,Results showed that grains were refined obviously after adding Ti in the steel， and the deoxidation products became the nucleuS of MnS or adhere around the AI2O3 inclusions， which were fine and distributed in the steeI dispersedly．This inclusions could induce the precipitation of intragranular needle—like fetrite frOm the austenite grains．having a microstructure refining effect． Key WOrds：oxide metallurgy；inclusions；intragranular ferrite：Ti 氧化物冶金 】是近年来采用的一项特殊技术，其 小而又互相交织的板条状组织物，板条之问相互连锁， 原理是通过加入合适的复合脱氧剂和采用合理的脱氧 分布在原奥氏体晶粒内。针状铁素体板条轴比为3：1或 制度来控制氧化物的性质，使钢中形成某种成分可控 5：1，板条问为大角度晶界，惯习面为与[1OO]、[1 lO]和 且弥散细小的氧化物颗粒，利用他们作为凝固时或固一 【331】相关的晶面。一方面晶内铁素体能使钢的晶粒细 固相变时的结晶核心，以改变钢的组织和晶粒度，使 小化，另一方