高Si／C、CE铸铁在生产中的应用.pdfVIP

学兔兔 Feb．2oo9 ·158· VoJ．58 NO．2 高Si／C、CE铸铁在生产中的应用 冯英宇 (沈阳职业技术学院．辽宁沈阳1 10045) 摘要：为消除铸铁件薄壁处的白口，提高铸件厚、薄壁处的强度、硬度，减少缩松缺陷，降低铸件残余应力，采取提高 Si／C值、CE方法生产高强度低应力铸铁。试验结果表明：用NSi／C和cE的铸铁取代低Si／c和cE铸铁，不仅应力低，而且相 对强度高、硬度高、断面均匀性好，铸件薄壁处不易出现白口，并成功地应用于压缩机铸件上，获得了较好的经济效益。 关键词：铸铁；硅碳比；碳当量；强度；硬度；残留应力 中图分类号：TGI11．5；TP391．9 文献标识码：A 文章编号：1001—4977(2009)02—0158—04 Application of High Si／C and CE Cast l r0n in Production FENG Yinq．yu (Shenyang Polytechnic College，Shenyang 1 1 0045，Liaoning，China) Abstract：To eliminate the chill structure of the thin-walled iron casting．improve the strength and hardness of the casting，reduce the shrinkage defect and decrease the residual stress，the high value of Si／C and carbon equivalent(CE)were adopted in production of high strength and low stress cast iron．The experiment results show that the cast iron with high Si／C and CE value。not only has the lower stress but also has the relative higher strength and hardness，the uniformjty 0f cross—section is good．and the chilI structure in the thin—wall is eliminated．1t has been successfully applied in the compressor castings． Key words：cast iron；ratio of silicon to carbon；carbon equivalent；strength；hardness；residual stress 压缩机铸铁件结构复杂，强度要求高，耐压性、 1 试验内容和方法 耐磨性、耐热性好。为了使铸件具有较高的强度、硬 度、致密性和无白口出现，几十年来形成了一套根据 1．1 现场试验 铸件壁厚的大小和性能要求来调整化学成分，使炉前 用中央送风热风冲天炉熔炼铁液，熔化率为5 t／Il， 得到不同的三角试片白口数这一控制铸件性能的方法。 出炉温度1 400～1 430℃。炉料为小岭生铁、薄片废钢和 这样就促使铁液牌号数量繁多，使工艺员、炉前工难 该厂回炉料。高硅碳比铸