309焊接用不锈钢盘条表面处理技术研究.pdfVIP

309焊接用不锈钢盘条表面处理技术研究 臧 震 胡俊辉 1 （宝山钢铁股份有限公司，上海 200940 ） 摘 要 不锈钢盘条退火以后，其表面的氧化皮由于其成分及结构的复杂性酸洗相对困难，309 焊接用不锈钢盘条 由于其成分与普通不锈钢不同，酸洗难度更大，通过分析普通不锈钢和309 不锈钢的氧化皮的结构，我们找到了两 者的区别，发现了309 焊接用不锈钢盘条酸洗困难的原因，通过盐浴处理及相应的酸洗处理技术，解决了309 不锈 钢酸洗相对困难的问题。 关键词 不锈钢盘条 酸洗 309 不锈钢 Surface Treatment Technology of 309 Stainless Steel Wire Rod for Welding Use Studying Zang Zhen Hu Junhui (Baoshan Steel Co., Ltd., Shanghai,200940) Abstract After stainless steel wire rod is annealed, the oxide skin on the surface is hard to be acid-washing because of the complexity of its composition and structure. Because of the composition of 309 stainless steel wire rod for welding use is different with ordinary stainless steel, so the 309 one is more difficult to be acid-washing, through analyzing the structure of the oxide skin of ordinary and 309 stainless steel, we find the difference between two kinds of stainless steel and also find the reason why 309 stainless steel wire rod is harder to be acid-washing than ordinary one to be. Through ARPAT and related acid-washing technique, we successfully solved the problem that 309 stainless steel is hard to be acid-washing. Key words stainless steel wire rod, acid-washing, 309 stainless 不锈钢盘条热轧或退火以后，其表面的氧化皮由于其成分及结构的复杂性，酸洗与一般钢材相比更加困难， 而且不锈钢钢种之间差异性较大，所以不锈钢盘条酸洗工艺复杂，是影响不锈钢盘条表面质量的重要因素。 1 不锈钢氧化皮特点 不锈钢中除铁之外一般含有铬、镍、硅、锰、钼等合金元素。这些元素在高温下氧化后生成的氧化物的 性质与铁的氧化物性质不同，使得不锈钢氧化后表面氧化皮的成分与结构变得复杂。不锈钢表面氧化铁皮主 要是在不锈钢的固溶过程中产生的。固溶温度必须能使钢材充分软化，再结晶完全。奥氏体不锈钢的再结晶 温度一般从900℃左右开始，大体上在1050～1200℃完成。 影响生成氧化铁皮的主要因素包括固溶的温度、时间和炉内气氛。在低温阶段加热时生成的氧化铁皮较 少，当加热温度超过850～900℃时,氧化铁皮增加速度很快，温度超过1200℃后，氧化铁皮则急剧增加。加 热温度愈高，时间愈长，生成氧化铁皮愈厚。而炉气中含有的氧化性气体O2 ，还原气体CO、H2 也是影响 1臧震，男，高级工程师，从事不锈钢材料开发，E-mail: zangzhen@ 8-66