航空用7475-T7351铝合金厚板耐腐蚀性能.pdfVIP

航空用7475-T7351铝合金厚板耐腐蚀性能

刘铭;李惠曲;陈军洲;李国爱;陈高红

【摘要】研究航空用7475-T7351铝合金厚板晶间腐蚀及剥落腐蚀性能,并利用金

相和透射电镜分析该合金的腐蚀行为.结果表明:7475铝合金无明显晶间腐蚀,剥落

腐蚀程度由表层的EA级递增至心部EC级.7475铝合金厚板发生剥落腐蚀主要是

由于合金为片状组织,同时晶界存在由电偶腐蚀构成的通路,晶界腐蚀产物体积膨胀

产生楔入力使晶间腐蚀沿着与表面平行的方向发展并逐步演变为剥落腐蚀.再结晶

程度由表层到中心逐渐降低,晶粒长宽比增加,剥落腐蚀倾向增大,导致表层到心部的

剥落腐蚀程度增加.%Theintergranularcorrosionandexfoliationcorrosion

propertiesof7475-T7351aluminumalloyplateforaviationwere

investigated,andthecorrosionbehaviorsofthealloywereanalyzedby

metallographicanalysis(MA)andtransmissionelectron

microscope(TEM).Theresultsshowthatnoobviousintergranularcorrosion

isobserved,butexfoliationcorrosiongradeof7475-T7351aluminumalloy

increasesfromEAonsurfacetoECinthecore.Theexfoliationcorrosionof

7475alloyplateismainlybecauseofthetypicallamellarstructure,andthe

pathwayformedbygalvaniccorrosionongrainboundary.Theexpansionof

grainboundarycorrosionproductvolumeproducesthewedging

force,makesintergranularcorrosiongrowalongthedirectioninparallel

withthesurface,andthengraduallyevolvesintoexfoliationcorrosion.The

degreeofrecrystallizationdecreasesgraduallyfromthesurfacetocenter,

andthegrainlength-to-widthradioincreases,whichinclinestoexfoliation

corrosionandleadstotheexfoliationcorrosiongradeincreasingfrom

surfacetocenter.

【期刊名称】《材料工程》

【年(卷),期】2017(045)009

【总页数】7页(P129-135)

【关键词】7475铝合金;晶间腐蚀;剥落腐蚀;再结晶

【作者】刘铭;李惠曲;陈军洲;李国爱;陈高红

【作者单位】北京航空材料研究院,北京100095;北京市先进铝合金材料及应用工

程技术研究中心,北京100095;北京航空材料研究院,北京100095;北京市先进铝合

金材料及应用工程技术研究中心,北京100095;北京航空材料研究院,北京100095;

北京市先进铝合金材料及应用工程技术研究中心,北京100095;北京航空材料研究

院,北京100095;北京市先进铝合金材料及应用工程技术研究中心,北京100095;北

京航空材料研究院,北京100095;北京市先进铝合金材料及应用工程技术研究中心,

北京100095

【正文语种】中文

【中图分类】TG146.2+1

早在20世纪30年代，人们就开始研究Al-Zn-Mg-Cu系合金，但由于该系合金

存在较为严重的腐蚀现象，限制了合金的进一步应用[1-3]，因此众多研究者通过

微合金化、高纯化、开发新合金以及新的热处理状态等方法，明显改善了合金的腐

蚀性能[4-6]。7475合金是1969年美国Alcoa公司在7075合金的基础上通过降

低F