现浇钢筋砼楼板裂纹防治.docVIP

现浇钢筋砼楼板裂纹防治 　　摘要：目前，现浇钢筋砼楼板裂纹成为困扰施工企业提高工程质量的一大难题。随着商品砼、流态砼的推广应用，这一问题更显突出，并得到了各界的关注。由于砼楼板裂缝原因很多，抓不住关键环节处理起来无法从根本上解决问题，每年施工单位在事后处理裂缝上投入了大量的人力和资金，造成许多不必要的 损失。所以必须采取措施减少开裂，以求满足使用功能要求。 　　关键词：楼板裂纹； 荷载； 变形； 时间因素； 原材料控制； 浇筑工艺； 养护 　　Abstract: At present, cracks in situ pouring reinforced concrete slab has become a major problem for the construction enterprises to improve the quality of project. With the popularization and application of commercial concrete and flow state concrete, the problem is more prominent, and has been concerned by public. As the causes for concrete floor cracks are multiple, processing it without the key aspects can not fundamentally solve the problem. In every year, the construction enterprises has put a lot of human and financial resources in the post-processing of cracks, resulting in numerous unnecessary losses. Therefore, measures must be taken to reduce cracking to meet the functional requirements. 　　Key words: floor cracks; load; deformation; time; control from raw material; pouring; maintenance 　　中图分类号：TU392.2 文献标识码：A 文章编号：2095-2104（2012） 　　一、原因分析 　　总的说来，砼楼板裂缝产生的原因不外两大方面：由荷载作用引起的；由变形变化引起 的 　　1.1荷载作用 　　由荷载作用引起的裂缝，通常也是由两个方面原因造成：由静动荷载的直接作用：由结构应力的作用。这两方面的裂缝控制主要依靠设计技术的不断发展，对“常规”不计算的、以及计算模型进行改进，通过设计技术水平的提高得到解决。 　　1.2变形的作用 　　有变形变化引起的裂缝，有温度、收缩、不均匀沉陷这几方面原因。通过王铁梦老师的研究结果，我们知道，这一类裂缝（以变形变化为主的）约占80%，而且随时间变化。因此在处理时应注意时间因素。 　　对于楼板，我们认为，温度和不均匀沉陷因素造成的裂缝较易于预防。关键在于控制收缩裂缝，这是砼自身特点造成的，是无法避免的，???且与时间关联密切，同样的方法，不同的时间去处理，效果截然不同。因此这是我们研究的重点。 　　1.3时间因素 　　我们知道造成收缩的原因主要在于砼孔隙中的水分，在砼拌合物中水分以化学结合水、物理——化学结合水、物理化学结合水三种形态存在。并随水化硬化过程的进行，而产生一系列的收缩变形；因其水化硬度的过程随时间变化，因此这种收缩变形也随时间变化。所以采取适当的措施，还要掌握好时机，才能达到控制的目的。 　　二、控制措施 　　砼裂缝的成因较复杂，涉及的方面较多，因此在制定技术措施上必须全面考虑。 　　1、 楼板施工前裂缝预控 　　1.1 、在认真做好图纸会审工作的基础上， 总承包施工单位应制定详细的楼板裂 裂缝的专项施工方案。专项施工方案应当由施工单位技术负责人审批，总监理工程师审查通过后实施。经批准的专项施工方案，不得随意变动，主要内容须包括：（ 1 ）、模板体系承载力、刚度与稳定性计算和防止立杆传力应力集中的构造措 施；（ 2 ）、模板周转套数；（ 3）、 钢筋位置、保护层厚度控制； （4 ）、电气线管位置、多层线管交叉控制； （5 ）、砼施工配合比的控制； （6）、 板厚控制；（7）、 混凝土浇捣控制；（ 8）、 混凝土初凝前找平与终凝前抹压时间控制；（ 9）、 混凝土养护方式与时间控制；（10 ）、终凝