毕业论文--聚苯乙烯微球.docVIP

摘 要 以苯乙烯为单体、2,2-偶氮二异丁基脒二盐酸盐（AIBA）为引发剂，在醇和水的反应中，采用分散聚合法制备聚苯乙烯微球，用扫描电镜观察了微球的形貌。考察了单体的浓度、AIBA的浓度、分散介质、醇水的比等因素对微球的粒径大小及其分布的影响。研究结果：苯乙烯和AIBA浓度的增加增大去离子水用量的增加，微球粒径会减小无水乙醇或异丙醇，微球分散不均一径明显增大。总之，引发剂和单体的浓度以及介质是影响微球及分布的主要因素 关键词：聚苯乙烯；分散聚合；粒径大小及分布；影响因素 ABSTRACT The polystyrene(PS)microspheres were prepared by dispersion polymerization of styrene in a mixture of water and alcoholusing AIBA as initiator. The surface morphorlogy of PS microspheres was observed by SEM. The effect of AIBA and monomer concentration, the dispersion medium and the volume ratio of alcohol and water on the particle size and the size distribution of PS microspheres were studied. The results show that the particle sizes increase with the increasing concentration of monomer and initiator. To increase the amount of deionized water, the particle size will correspondingly decrease. To transform the dispersion medium from methyl alcohol to ethyl alcohol or isopropanol, the particle size will obviously increase and the PS microspferes will disperse inhomogenously. In a word,the concentration of AIBA and styrene and dispersion medium are the main factor that affected the size and distribution of polystyrene microspheres. Keywords: polystyrene microspheres; dispersion polymerization; particle size and size distribution; influencing factors 目 录 第一章 绪论 1 1.1 分散聚合的基本概念 1 1.2 分散聚合的研究背景 1 1.3 分散聚合的各组分 2 1.4 水溶性偶氮类引发剂的介绍 2 1.5 分散聚合机理研究 3 1.5.1 分散聚合的稳定机理 3 1.5.2 分散聚合的成核机理 4 1.6 分散聚合与其他制备聚合物微球方法的比较 5 1.7 分散聚合动力学研究 6 1.8 分散聚合技术的应用 7 1.9 课题的提出 7 第二章 实验部分 8 2.1 试剂 8 2.2 实验装置 8 2.3 PS微球的制备 9 2.3.1 聚合条件 9 2.3.2 试剂的提纯 9 2.3.3 单分散微球的制备 9 2.4 PS微球的表征 9 2.4.1 扫描样品的制备 10 2.4.2 PS微球的粒径方程 10 2.4.3 平均粒径和粒径分布 10 第三章 结果与讨论 11 3.1 聚合过程 11 3.1.1 反应现象 11 3.1.2 聚合分析 11 3.2 反应原料组成对粒径及粒径分布的影响 12 3.2.1 引发剂浓度对微球粒径大小及粒径分布的影响 12 3.2.2 单体浓度对微球粒径大小及粒径分布的影响 14 3.2.3 醇/水比例对微球粒径大小及粒径分布的影响 16 3.2.4 分散介质种类对微球粒径大小及粒径分布的影响 18 3.3 聚苯乙烯微球的成核机理研究 20 第四章 结论 22 参考文献 23 致谢 24 第一章 绪论 1.1 分散聚合的基本概念 分散聚合是一种新型的聚合方法，于20 世纪70 年代初由英国 ICI公司