氧化锌论文：氧化锌可见区发光机理研究进展 【中文摘要】ZnO是一种具有六角纤锌矿结构的直接带隙宽禁带半导体材料,室温下的禁带宽度为3.37 eV,激子束缚能达60 meV,保证了在室温下较强的激子发光。而且ZnO由于它优异的光电特性,在发光(激光)二极管、紫外探测器、气敏元件、平板显示器等领域它都有很好的应用前景。通常ZnO薄膜的发光可分为近带边(NBE)紫外发光和深能级(DL)发射,虽然ZnO可见区发光机理是氧化锌研究当中一个十分重要的问题。但由于ZnO材料本身的特点,虽然许多研究小组对此进行了广泛的研究,但到目前为止仍然没有统一的观点。本文主要围绕应用量子限制效应、带边调制及表面修饰等不同方法对ZnO可见区发光机理的研究进行了综述。 【英文摘要】ZnO is a kind of direct wide-gap semiconductor, which has hexagonal wurtzite crystal structure and opto-electronic and piezoelectric characteristics. At room temperature,its band gap is 3.37 eV, exciton binding energy may reach 60 meV, ensuring its intense excitonic luminescence. Moreover, in virtue of the excellent opto-electronic characteristics, ZnO is promising for applications in the fields of LED, UV detector, gas sensor and flat plate display, etc.Commonly, the luminescence of ZnO includes near band edge (NBE) UV emission and deep level (DL) related visible emission. Although the visible luminescence mechanism of ZnO is of great importance in ZnO research, and has been intensively investigated by many groups, using methods such as quantum confinement, band edge modulation and surface modification, etc., no unambiguous conclusion has been reached up to now because of its complicated characteristics. In this thesis, the research progress on the visible luminescence of ZnO materials was reviewed in detail. 【关键词】氧化锌 发光机制 量子限制 带边调制 表面修饰 【英文关键词】zinc oxide visible luminescence mechanism quantum confinement band edge modulation surface modification 【备注】索购全文在线加好友：.3.8848 同时提供论文写作一对一指导和论文发表委托服务 【目录】氧化锌可见区发光机理研究进展 摘要 4-5 Abstract 5 第一章 引言 7-15 1.1 ZnO 的基本性质 8-11 1.2 ZnO 的制备方法 11-13 1.3 ZnO 材料的应用 13-14 1.4 本论文的研究目的 14-15 第二章 氧化锌的发光性质 15-18 2.1 氧化锌发光的基本性质 15-16 2.2 紫外近带边发射 16-17 2.3 可见区发射 17-18 第三章 氧化锌可见区发射机理研究 18-34 3.1 氧化锌可见区发光研究简介 18-19 3.2 量子限制方法研究 ZnO 可见区发光机理 19-23 3.3 带边调制方法研究 ZnO 可见区发光机理 23-26 3.4 表面修饰方法研究 ZnO 可见区发光机理 26-28 3.5 其它方法 28-34 第四章 结论 34-35 参考文献 35-41 致谢 41