异种材料电阻点焊毕业论文终稿.docVIP

不锈钢与低碳钢点焊工艺与接头分析 学生姓名： 班级： 指导老师： 摘要：本论文主要研究低碳钢与不锈钢的焊接工艺，即异种材料的焊接工艺研究，为异种材料和钢的焊接提供理论基础和试验基础。不锈钢及中含有合金元素和杂质，在焊接过程中易形成各种低熔点共晶体和脆性化合物，严重削弱了金属在高温时的晶间结合力。由于导热系数比不锈钢大得多，需采用大功率热源，因此热影响区宽，使接头承受较大应力，焊缝易产生热裂纹。通过焊接检验可知，焊缝具有良好的性能；经金相检验，焊缝内部组织均匀Abstract This paper studies in low carbon steel and stainless steel welding technology, Namely dissimilar material of welding technology research for the dissimilar materials low carbon steel and stainless steel welding to provide the theoretical foundation and experimental basis. The mainly welding process is tungsten inert gas arc welding . Stainless steel and low carbon steel alloy containing elements and impurities, in the welding process in the formation of low-melting-eutectic and brittle compounds, severely weakening the metal in the temperature of crystallization binding force. Thermal conductivity of low carbon steel due to greater than stainless steel, to use high-power heat, the heat-affected zone width, the larger joints under stress, thermal weld cracks easily. Through welding inspection, we can see that Weld has a good performance, the metallographic examination, the internal organization of uniform weld. Key words： low carbon steel stainless steel welding technology metallographic analysis 目 录 第1章 绪 论 1.1 课题研究的目的及意义 1 1.2 焊接技术概述 1 第2章 不锈钢、低碳钢的焊接基础理论 2.1 焊接冶金过程特点 4 2.2 焊接接头的组织与性能 4 2.2.1 对焊缝金属的研究 5 2.2.2 熔合区的构成与特点 6 2.2.3 热影响区 7 2.3 低碳钢热影响区的组织分析 8 2.4 低碳钢和不锈钢的焊接性理论分析 8 2.4.1 金属可焊性概念 8 2.4.2 金属焊接性化学分析方法 9 2.5 不锈钢的焊接性分析 10 2.6 低碳钢的焊接性分析 11 2.7 低碳钢和不锈钢在国内外的发展现状 14 2.8 异种金属材料焊接存在的技术问题及缺陷 14 第3章 实验方法材料与设备 3.1 引言 16 3.2 试材料选择 16 3.3 实验设备 18 第4章 实验结果及分析 4.1 焊接接头金相组织分析内容 19 4.2 实验数据 19 4.3 焊接中存在的问题 20 4.4 金相分析 20 4.4.1 金相组织分析 20 4.4.2 焊点显微硬度分布 21 4.4.3 失效焊点断口分析 22 4.4.4 接头分析 22 4.4.5 热影响区 23 结 论 25 参 考 文 献 26 致 谢 27 第1章 绪 论 1.1 课题研究的目的及意义 随着经济的迅速发展和科学技术的不断进度，新材料、新工艺、新设备不断涌现，对零部件的性能提出了更高的要求。异种金属材料的焊接技术已逐步被熟练掌握并广泛应用到化学工程、航空航天、造船、核工程、异种材料等各个领域，如航天发射架装置、齿轮轮齿与轮辐材料的链接等应用。因此，异种材料焊接技术越来越受人们的重视。采