铸钢件内冷铁设计与应用的探讨.pdfVIP

学兔兔 铸钢件内冷铁设计与应用的探讨 徐尔灵，罗永扬，叶建军，刘启平 (广东省韶铸集团有限公司，广东 韶关 512031) 摘要：探讨了现有文献中铸钢件熔合内冷铁最大直径计算方法存在的问题，针对内冷铁设计和 应用中常忽视的几个重要因素提出了解决思路，并介绍了熔合内冷铁工艺应用的成功经验。 关键词：内冷铁；铸钢件；工艺设计 中图分类号：TG244 ．3 文献标识码：B 文章编号：1673—3320(2013)03—0044—02 Discussion on Design and Application of Internal Densener for Steel Casting Xu Erling，Luo Yongyang，Yie Jianjun，Liu Qiping (Guangdong Shaoguan Foundry and Forging Group Co．，Ltd Shaoguan 51 2031，Guangdong，China) Abstract：Some problems in current references about the maximum diameter of internal densener melted in steel castings were discussed．Also regarding to several important issues often neglected in design and application of internal densener,the solutions were presented and the successful experiences in process application were introduced． Key words：internal densener；steel casting；process design 铸钢件常采用内冷铁以缩小铸件整体或局部 dm =0．1tuMr 0 (1) 热节模数，控制凝固顺序，减小冒口体积和消除 式中： 为欲加入内冷铁铸件的实用模数，mm； 缩孔、缩松缺5臼【 】。内冷铁的激冷作用比外冷铁 为钢液过热度，℃。 强[2]。科学规范地应用内冷铁，除满足工艺需要 假Pat =1O0℃，Mr=l0 mm，计算出dm 一 外，还能细化晶粒和减小铸造应力，减少热裂纹 63 l mm；如猜测 单位有误，按常规单位Mr= 的产生，进而提高工业出品率，降低铸件生产成 2 cm代入，则计算出dm。 一34．8 mm。以上两个假 本。所以内冷铁成为国内大中型铸钢生产厂家不 设计算得出的熔合内冷铁直径都大大超过铸件实 可缺少的工艺手段。而现有铸造工艺指导性书籍 用模数Mr，说明该公式计算得到的数据显然值得 中关于内冷铁的应用描述不多，使得工程技术人 商榷，不能准确指导内冷铁的设计。 员在设计时缺少依据。由于内冷铁的设计和应用 所带来的一系列问题，严重影响了产品的质量。 2 熔合内冷铁最大直径查表法 本文结合多年来对于内冷铁设计基础问题的探索 文献[1】给出了熔合内冷铁最大直径的图表 心得和应用经验，与大家共同探讨交流。 法，如图1所示。