铸钢件生产中推广酯固化水玻璃自硬砂的可行性.pdfVIP

学兔兔 Sep．2009 铸 造 FOUNDRY ·965· VoI．58 No．9 铸钢件生产中推广酯固化水玻璃自硬砂的可行性 金广明，魏 甲，张俊法，刘洪涛 (沈阳汇亚通铸造材料有限责任公司，辽宁沈阳1 10136) 摘要：结合铸钢件生产工艺现状，详细论述了酯固化水玻璃自硬砂技术创新点，推广应用情况，发展趋势。论证了在 装备制造业的铸钢件生产中推广该项技术的可行性及此项技术对改善铸件质量、提高劳动生产率、降低成本、减少固 废排放、保护生态环境的意义。 关键词：水玻璃；自硬砂；酯固化；铸钢件 中图分类号：TG222 文献标识码：B 文章编号：100l一4977(2009)09-0965-04 Feasibility of Generalizing Ester Cured Sodium Silicate Sand in Steel Castings Production JIN Guang—ming，WEI Jia，ZHANG Jun—fa，LIU Hong—tao (Shenyang Hyaton Foundry Material Co．，Ltd．，Shenyang 1 10136，Liaoning，China) Abstract：Combined with existing production conditions of steeI castings，the technical innovation and application as welI as developmental trend of ester cured sodium silicate sand were discussed in detail．It was demonstrated that the feasibility of generalizing this technology in producing steel castings for the equipment manufacturing industry and its significance in improving the casting quality and Iabour productivity．reducing costs and the emission of solid waste，and protecting the ecological environment． Key words：sodium silicate；self-hardening sand；ester cured；steeI casting 我国是装备制造业大国，而铸造是装备制造的基础 长远考虑，高耗能、高污染的物质将逐步被替代。CO： 产业。据2007年末统计，我国年产铸件3 126．9万t， 水玻璃砂已在我国应用几十年，是一种传统的铸造技 其中铸钢件404．7万t[q，是世界第一铸造大国。铸造 术，尽管其溃散性差、旧砂不能再生回用、生产铸件 又是排污严重的产业，我国每生产l t合格铸件，大约 质量粗糙，但由于其来源广，价格便宜，无毒无味， 要排放粉尘50 kg，废气l 000～2 000 m ，废渣300 kg， 很多企业生产铸钢件仍采用该工艺。加入WTO之后， 废砂1．3～1．5 t。这些固体废弃物中往往含有大量污染 装备制造业面临国内、国外市场需求，铸件质量差直 物，其中包括：苯、苯酚、呋喃、甲醛、Ot．苯丙芘、 接影响机械装备的质量和市场竞争力。火车提速后， 二恶英、NaOH、KOH等。随着雨水冲刷，有些物质 要求车辆铸钢件优质、重载、安全，铸件材质由普通 流入地表，破坏土壤结构，