近终形薄带连铸无取向硅钢的研究进展 刘海涛 孙 宇 刘振宇 曹光明 李成刚 邱以清 王国栋 (东北大学轧制技术及连轧自动化国家重点实验室, 沈阳 110004) 摘 要 本文简要介绍了薄带连铸3.2%Si+0.7%Al 无取向硅钢的必威体育精装版研究进展。研究表明，通过调整熔池内钢水的 过热度可以实现对铸带初始组织、织构的有效控制。在较高的过热度条件下，获得了具有显著{001}uvw织构的 柱状晶铸带。柱状晶铸带经冷轧和退火处理后，与常规产品相比，晶粒尺寸较小，有利的{001}uvw织构显著增 强，有害的{111}uvw织构显著减弱，B50 提高0.04T 以上。1 关键词 薄带连铸 无取向硅钢 织构 磁感应强度 Recent Progress on Near-net Shape Thin Strip Casting Non-oriented Silicon Steel Liu Haitao Sun Yu Liu Zhenyu Cao Guangming Li Chenggang Qiu Yiqing Wang Guodong (State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang, 110004) Abstract In the present work, the recent progress on near-net shape thin strip casting 3.2%Si+0.7%Al non-oriented silicon steel was briefly described. It was found that the initial microstructure and texture of the as-cast strip could be controlled by changing the superheats in the melt pool. In the case of high superheat, a columnar as-cast strip with pronounced {001}uvw texture was produced. And after cold rolling and annealing, the sheet showed smaller grain size, much stronger desirable {001}uvw texture and much weaker {111}uvw texture in comparison with the conventional sheet, thus the B50 was increased by more than 0.04T. Key words strip casting, non-oriented silicon steel, texture, magnetic induction 1 引言 用于制造各种电动机、发电机铁芯等产品的无取向硅钢是电力、电子、军事和民用工业领域重要的软磁 材料，要求具有较高的磁导率和较低的铁损。这两项性能指标都在不同程度上依赖于材料内部晶体的择优取 向—织构。理想的晶体织构为{001}uvw面织构[1]，因为它是各向同性且难磁化方向{111}不在轧制平面内。 但是，在实际中并不能得到这种单一的面织构，人们只能设法强化{001}uvw织构和弱化{111}uvw织构 以得到较好的磁性。 薄带连铸是以液态金属为原料、以旋转的冷却辊为结晶器，用液态金属直接生产薄带材的技术，是一种 将快速凝固与加工变形融为一体的近终形成形技术。最近20 年，薄带钢连铸技术获得了较快发展，美国的 纽柯钢铁公司已经开始利用薄带连铸技术生产低碳钢商品带材[2]，薄带钢连铸产业化的发展前景逐渐明朗。 1国家自然科学基金, 中国博士后基金(201