马钢大型转炉炼钢工艺正常化的途径.pdfVIP

马钢大型转炉炼钢工艺正常化的途径1 1 2 1 2 2 杨文远 徐小伟 王明林 邓 勇 朱伦才 （1.钢铁研究总院, 北京 100081 ；2.马鞍山钢铁公司，马鞍山 243000 ） 摘 要 马鞍山钢铁公司第四炼轧厂有300 吨复吹转炉两座，投产初期生产不正常。通过改进氧枪喷头参数，开展 转炉炼钢的基础研究，优化吹氧、造渣制度和规范吹炼操作等措施，经过两年多的生产实践，使转炉炼钢操作正常 化，能够满足生产低碳优质深冲钢的技术要求。 关键词 转炉炼钢 氧枪喷头 吹氧 Way to Steelmaking Process Normalization of Large Converter in Ma’anshan Iron and Steel Co., Ltd. Yang Wenyuan1 Xu Xiaowei2 Wang Minglin1 Deng Yong2 Zhu Luncai2 (1.Central Iron and Steel Research Institute, Beijing, 100081; 2. Ma’anshan Iron and Steel Co., Ltd., Ma’anshan, 243000) Abstract There are two 300t top and bottom blowing converters in Maanshan Iron and Steel Co., Ltd which are abnormality when they put into production at beginning. After more than two years of production practice, converter steelmaking operation are normalized and satisfied the production of low carbon deep drawing steel requirements through improving oxygen lance nozzle parameters, basic research in steelmaking, optimizing the oxygen blowing and slagging system and regulating the converter operation. Key words converter steelmaking, oxygen lance nozzle, oxygen blowing 1 引言 马鞍山钢铁公司第四炼轧厂有2 座公称容量300 吨转炉。该厂以优质低碳深冲钢为主要产品。四炼轧转 炉投产时操作工人主要来自本公司第二炼钢厂。投产后出现炼钢操作不能适应大型转炉的要求。表现为吹炼 操作不稳定，终渣氧化铁高，喷溅粘枪严重，枪龄短等问题。马鞍山钢铁公司与钢铁研究总院合作，根据四 炼轧情况，吸取国内、外大型转炉经验，通过改进转炉氧枪喷头参数、优化供氧、造渣制度和统一工人操作， 经过两年多的共同努力使马钢四炼轧的转炉炼钢操作达到国内大型转炉的先进水平。 2 转炉炼钢工艺优化所进行的几项工作 2.1 转炉氧气管道压力损失测定 压力损失（ΔP ）指由氧气管道切断阀后取压点工作氧压（P ）与氧枪喷头入口处压力（P ）之差（ΔP= 1 0 P − P ）。通过实测得出管道压力损失与工作氧压的关系为： 1 0