15NiCuMoNb-4无缝钢管热处理工艺研究.pdfVIP

15NiCuMoNb5-6-4 无缝钢管热处理工艺研究1 张宝惠 何 彪 郭火星 肖功业 赵庆权 张俊萍 王国亮 曹金荣 吴光煦 （天津钢管集团股份有限公司，天津 300301 ） 摘 要 本文研究了热处理工艺对15NiCuMoNb5-6-4 性能的影响。发现随回火温度的升高硬度先降低后升高，强 度逐渐降低；随回火保温时间的延长硬度逐渐降低，冲击韧性逐渐升高；结果表明，该钢的最佳回火工艺为回火 温度630～660℃，保温时间不少于90min，此时钢具有最佳的综合性能。 关键词 15NiCuMoNb5-6-4 热处理工艺 性能 Research on Heat Treatment of 15NiCuMoNb5-6-4 Seamless Pipe Zhang Baohui He Biao Guo Huoxing Xiao Gongye Zhao Qingquan Zhang Junping Wang Guoliang Cao Jinrong Wu Guangxu (Tianjin Pipe (Group) Corporation, Tianjin, 300301) Abstract The influence of heattreatment on property of 15NiCuMoNb5-6-4 is researched. It is found that hardness descend and then raise, and strength gradually descend when tempering temperature ascend. Hardness descend and toughness raise when tempering time add. The best tempering technics of this steel is that tempering temperature is 630~660℃, and preservation time is at lest 90 minute. It can be reached best integrated property. Key words 15NiCuMoNb5-6-4, heattreatment technics, property 1 引言 15NiCuMoNb5-6-4 属于欧标EN10216-2 标准的钢种。它是在碳锰钢的基础上添加Ni-Cu-Mo-Nb 等合 金，从而起到了细晶强化以及沉淀强化的效果[1]，大大提高了该钢种的高温强度以及持久强度。该钢的特 点是强度高，使用温度为400 ℃，也可用作管壁温度达500℃ 的高应力管道，或用作高参数火力发电机组， 广泛应用于超临界机组中的锅炉汽包、汽水分离器、集箱、蒸汽发生器、蒸汽管道和核电设备等高压部件。 本文通过对15NiCuMoNb5-6-4 的成分特点进行分析，对热处理工艺进行了研究，得到了最佳热处理工 艺。 2 试验方法 具体制管工艺为：电炉—LF—VD—模铸—锻造—退火—管坯加热—穿孔—PQF 连轧—定径—探伤， 规格为φ323.9×14.2mm。化学成分见表1。 张宝惠，男，大本，高级工程师，主要从事金属材料及轧管工艺研究，现任技术中心党委书记，zhangbh@tpco.cn 第八届（2011 ）中国钢铁年会论文集 表 1 试验所用试样化学成分（wt/%） 元素 C Si Mn P S Cr Ni Cu Mo Nb Altot 标准 ≤0.17 0.25～0.50 0.80～1.20 ≤0.025 ≤0.020