北营炼铁厂6号高炉无砖衬全喷补开炉实践.pdfVIP

北营炼铁厂 6 号高炉无砖衬全喷补开炉实践 陈东方 （本钢集团北营炼铁厂，本溪 117017 ） 摘 要 北营炼铁厂6 号高炉中修后对炉腹以上无砖衬部位进行了喷补造衬，通过对喷补料脱落量的精确评估和开 炉方案的精心制作与严格执行，尤其是对喷补反弹料的造渣处理，避免了开炉过程中常见的烧风口休风现象，降低 了炉前劳动强度，加快了炉内冶炼进程，使得6 号高炉顺利开炉并快速达产，取得了较好的技术经济指标，创造了 较大的经济效益。1 关键词 开炉 喷补 经济效益 # The Practice of Blowing-in of 6 BF of Beiying Iron Works after Whole Gunning Without Brick Chen Dongfang (Beiying Iron Works of Benxi Iron Steel Group Co., Benxi, 117017) # Abstract 6 BF of Beiying iron works in to repair the hearth of the furnace after abdominal above without brick linning up the parts of spray made ling. Through to spray the amount of material for accurate assessment and fall off the furnace of elaborate scheme and the strict execution, especially for spray fill material slagging rebound processing, to avoid the furnace in the process of XiuFeng tuyere burning common phenomenon, reduce the labor intensity, speed up before furnace inside the furnace process, make smelting blast furnace and smooth 6# rich the target of production fast, and achieved good technical and economic indexes, and create a larger economic benefits. Key words blowing-in ，gunning，economic benefit 1 引言 3 北营炼铁厂6 号高炉于2002 年5 月29 日开炉，有效炉容420m ，配备14 个风口、1 个铁口和 1 个渣 口。2002～ 2010 年生产期间由于原燃料条件极差，其间高炉频繁结瘤，为处理结厚、结瘤多次休风炸瘤， 导致炉身砌砖全部脱落。由于炉龄较长，炉底、炉缸炭砖侵蚀严重，2010 年6 月15 日停炉中修，更换炉底、 炉缸炭砖。由于某种原因，公司没有炉腹以上部位砌砖计划，铁厂于是采取喷补造衬方案来重塑炉型和保护 冷却壁。通过借鉴以往喷补与开炉先进经验，制定和执行周密精细的开炉方案，北营炼铁厂6 号高炉在中修 喷补后于2010 年7 月22 日顺利开炉，并迅速达产。开炉后3 个月，各冷却壁工作正常，高炉生产取得了较 好的技术经济指标。 陈东方（1979-），男，毕业于武汉科技大学，冶金工程专业，现职务为北营炼铁厂高炉主管工程师，助理工程师职称，从事炼铁工艺管理，