V、N微合金化对高碳钢77B等温组织的影响.pdfVIP

V、N 微合金化对高碳钢 77B 等温组织的影响 1 2 王勇围 马党参 （1. 首钢技术研究院，北京 100043 ；2. 钢铁研究总院结构材料所，北京 100081 ） 1 摘 要 对未微合金化和 V 、N 微合金化的高碳钢 77B 进行了等温和奥氏体热变形后等温处理，结果表明：等温处 理的 V 、N 微合金化 77B 钢中，V(CN) 的析出方式分为相间析出和弥散析出，珠光体片层间距比未微合金化的77B 宽，但珠光体团尺寸细化，经热变形等温处理后珠光体团进一步细化，这与 V(CN) 的形变诱导析出阻碍奥氏体回复 再结晶，提高了珠光体的形核率有关。 关键词 77B V 、N 微合金化 沉淀析出 Effection of V、N Micro-alloyed on Microstructure of High Carbon 77B by Isothermal Treated Wang Yongwei1 Ma Dangshen2 ( 1. ShouGang Research Institute of Technology, Beijing 100081; 2.Institute for Structural Materials, Central Iron and Steel Research Institute, Beijing 100081) Abstract High carbon steel 77B with and without V 、N micro-alloyed were isothermally treated and austenite thermally deformed then isothermally treated. Results show that: V(CN) can be inter-phase and randomly precipitated in 77B with V、 N micro-alloyed after isothermally treated, but lamellar space of pearlite and peatlite cluster are broader and further fine than 77B steel without micro-alloyed. Pearlite cluster can be refined further after thermally deformed then isothermally treated, the reason include that deformation induced precipitation of V(CN) delayed the recovering and re-crystallization of austenite grain, and nucleating ratio of pearlite improved correspondingly. Key words 77B ，V 、N micro-alloyed ， precipitating 高碳钢预应力线材 77B 盘条常用于生产高强度预应力钢绞线，是高级硬线钢的代表钢种[1]，已广泛用于 建筑、桥梁、交通、水利等现代化重要工程。近几年随着产量的大幅度增加，在装备上也越来越先进，尤其 是近十几年新上的 stelmore 生产线，是世界上非常先进的设备和工艺。目前，我国已成为世界上拥有高速线 材生产线最多、产量最大的国家。V 是钢中常用的微合金化元素，加N 后能促进 V （CN ）的析出，提高材 料的强韧性。连续冷却可以看作无数个等温过程的叠加，本文通过盐浴等温和热变形+等温试验，结合金相， 透射（TEM ）电镜等分析方法初步探讨了V （CN ）在高碳钢77B 中的析出和对77B 钢组织的影响，为进一