60Si2Mn弹簧扁钢断面缺口的解决办法.pdfVIP

60Si2Mn 弹簧扁钢断面缺口的解决办法 陈 明 黄乐枧 陈苏勤 张曙光 （方大特钢科技股份有限公司，南昌 330012 ） 1 摘 要 电炉在高效化生产60Si2Mn 弹簧钢过程中，由于电弧炉冶炼时碳与炉渣的控制不当、LF 精炼炉埋弧效果 差、连铸保护浇注措施不到位等三方面原因，致使 60Si2Mn 弹簧钢中N 含量高（140～180ppm）。[N]高的 60Si2Mn 铸坯轧制成扁钢后，在剪切下料过程中，极易发生断面缺口现象（严重的碎裂）。本文主要针对这一质量问题，提 出了解决办法。 关键词 60Si2Mn 弹簧扁钢 N 含量 Resolution Measures for Breakup of 60Si2Mn Spring Flat Steel Chen Ming Huang Lejian Chen Suqin Zhang Shuguang (FangDa Science and Technology of Special Steel Co.,Ltd，NanChang 330012 ，JiangXi ，China) Abstract As the control of carbon and slag in EAF, the effects of submerged arc operation in LF and the measures of protection casting in CC, nitrogen content in 60Si2Mn spring steel was high (140~180ppm) in high efficient Steelmaking of EAF. The 60Si2Mn spring flat steel of high nitrogen had the breakup even smash problem during the cutting process. This article mainly put forward the resolution measures for this quality problem. Key words 60Si2Mn, spring flat steel, nitrogen content 1 前言 随着超高功率偏心底电弧炉工艺（部分铁水配料，熔炼过程燃料助熔、自动氧枪富氧操作，喷碳粉泡沫 渣）的日趋成熟，加上精炼、连铸等配套设施的完善，电炉高效化生产已成必然。 我公司电炉主要生产牌号 60Si2Mn 为主的弹簧钢。在电炉高效化生产过程中，60Si2Mn 弹簧钢铸坯轧 制成扁钢后，剪切下料时经常发生断面缺口现象。经对比检测发现，凡出现断面缺口的 60Si2Mn 扁钢，[N] 含量高（140～180ppm）。针对 60Si2Mn 扁钢断面缺口这一质量问题，我们主要采取了降氮、固氮、控制 60Si2Mn 固溶强化元素C 与 Si 成分和降低轧制温度等四方面措施，取得了实效。 2 降氮的工艺措施 从电弧炉冶炼、偏心底出钢到 LF 炉精炼、连铸浇注的整个生产过程中都存在增氮现象。经对钢水分阶 段检测分析，我们发现在电弧炉冶炼、LF 炉精炼、连铸浇注三个工序的生产过程中，如果工艺操作不当， 则增氮严重。 陈明（1978-），男，工程师，主要从事质量管理及产品研发，chenming0823@163.com 60Si2Mn 弹簧扁钢断面缺口的解决办法 2.1 钢水氧化过程碳与炉渣的控制 2.1.1 碳的控制 电炉高效化冶炼弹簧钢，特别是冶炼60Si2Mn 弹簧钢，其关键点是控制废钢全熔后的[C]含量。碳高， 不但影响生产效率和经济效益；操作时还易出现脱碳速度过大，造成炉渣喷溅，钢液裸露，吸气严重。碳低， 则不利去除钢液中的气体（氢和氮）及夹杂物。 （1）电弧炉的主要技术特征：我公司电弧炉的变压器容量 15MV ·A ，平均实际出钢量 28t，平均功率 水平 535.7kV ·A/t 。 （2 ）熔清后的[C]与出钢前的终点[C]的控制：由于部分铁水配料、富氧