热轧工艺对冷轧双相钢组织性能的影响.pdfVIP

热轧工艺对冷轧双相钢组织性能的影响 梁 轩 阳代军 （首钢股份技术研究院，北京100083） 摘 要 研究了热轧卷取温度对气冷退火冷轧双相钢组织性能的影响，并采用 ThermoCalc 相图计算分析，结果表 明，热轧高温卷取一方面可使冷轧退火后得到相对粗大的晶粒，有利于降低双相钢的屈服强度，另一方面高温卷取 产生的晶界 Mn 偏聚可以增加退火冷却时奥氏体的淬透性，提高双相钢的抗拉强度。这使得热轧高温卷取的冷轧气 冷退火双相钢具有更低的屈强比和更好的塑性。 1 关键词 双相钢 卷取温度 力学性能 显微组织 Effect of Coiling Cemperature on Microstructure and Properties of Cold Rolled Dual Phase Steel Liang Xuan Yang Daijun （Shougang Research Development Center, Beijing, 100083） Abstract The effect of coiling temperature on microstructure and mechanical properties of cold rolled DP steel was investigated by means of experimentation and ThermoCALC computation, and the results showed that the high coiling temperature can result in coarse ferrite grains which is beneficial for the decreasing of yield strength. On the other hand, the resulting Mn enrichment at the grain boundary can improve the hardenability of austenite during the course of gas cooling, and result in more martensite upon the gas jet cooling which can increase the tensile strength of DP steel. Therefore, the high coiling temperature can ensure the lower yield ratio and better ductility for the continuous annealed DP steel with gas jet cooling, and it is good for forming. Key words dual phase steel, coiling temperature, mechanical properties, microstructure 随着现代汽车工业的发展，减重节能成为大势所趋。冷轧双相钢[1~2]具有低屈强比、无屈服延伸、初 始加工硬化速率高以及高强度高塑性等特点，有助于汽车工业减重节能，是一种优良的汽车结构用钢。 双相钢属于铝镇静钢，冶炼浇铸决定了其成分和铸态组织，但要得到双相钢最终的优异性能则必须合理 地控制生产工艺（包括热轧、冷轧、连续退火），因为生产过程的每一步都与最终产品的性能密切相关。关 于连续退火工艺对冷轧双相钢力学性能的影响，前人已有大量的研究[3~6]，但有关热轧工艺对冷轧双相钢 组织性能的研究很少，热轧工艺主要包括加热温度、终轧温度、卷取温度等，其中卷取温度是影响热轧板显 微组织的关键因素。本文主要研究热轧卷取温度对连续退火双相钢显微组织及力学性能的影响。 1 材料及试验方法 试验用钢由 50kg 真空炉冶炼，冶炼后锻造成坯，坯