热轧精轧机工作辊局部磨损问题研究 王文广 杨孝鹤 艾矫健 （首钢技术研究院，北京 100043 ） 摘 要 本文以某厂 1580 热轧精轧机为研究对象，针对精轧机工作辊局部磨损问题进行了分析，根据工作辊局部 磨损曲线的特点和轧件对工作辊的磨损机理，揭示了此类工作辊局部磨损的形成原因，同时就此类磨损对产品板廓 的影响进行了分析。之后，结合此热轧机组设备和生产工艺特点，开发了利用CVC 轧机工作辊可窜动特点的工作 辊 “Z”形窜辊策略，有效的解决了精轧机工作辊局部磨损问题，提高产品质量。 关键词 工作辊 局部磨损 板廓 周期性窜辊 Study on Partial Wear of Finishing Work Roll for HSM Wang Wenguang Yang Xiaohe Ai Jiaojian (Shougang Research Institute of Technology, Beijing, 100043) Abstract The finishing mill of one 1580mm HSM was the object to be studied. The main job was to analyze the issue of partial wear of finishing work roll, According to the feature of the worn curve of the work roll and the principle of the wear, the reason for such kind of wear of the work roll was uncovered, and profile of product made by the partial wear of work roll was also analyzed. Then, combining with the characteristic of the equipments and technology, new side shift mode, called Zig-Zag mode, was exploited using the feature of CVC, which can modify the problem of partial wear of finishing work roll, and improve the quality of the product. Key words work roll, partial wear, profile, Zig-Zag mode 众所周知，在热轧生产中精轧机工作辊的磨损是不可避免的，工作辊磨损一方面会影响工作辊的使用寿 命，另一方面则会改变工作辊辊形，进而影响产品板形。因此，关于工作辊磨损问题的研究集中在降低磨损 量和减小工作辊磨损对辊形影响两个问题上。热轧精轧机工作辊的局部磨损就是一种对工作辊辊形有恶劣影 响的磨损现象。本文以某厂热轧精轧机为例，就工作辊局部磨损的产生原因及其控制技术进行了研究。 1 工作辊局部磨损及成因分析 在热轧轧制过程中，精轧机工作辊与轧件接触区发生磨损是不可避免的，而局部磨损则是指在工作辊的 小范围内磨损量明显大于其它部位，在工作辊磨损曲线上形成明显尖点的现象，如图1 所示为某厂1580 热 轧精轧机工作辊磨损曲线，在与轧件边部接触的部位存在明显局部磨损。 8-424 第八届（2011 ）中国钢铁年会论文集 图1 工作辊磨损曲线 ［ ］ 1~3 精轧机组工作辊的磨损可分3 种 ：(1) 机械或摩擦磨损，是由于工作辊同轧件及支撑辊表面相互作 用而引起的摩擦造成的；(2) 化学磨损是辊面与周围介质的相互作用，表面膜的形成和破坏的结果；(3) 热 磨损是由于高温作用和轧辊在放置过程中表面层温度剧烈变化而导致的。 根据上