武钢板坯连铸中间包自动开浇技术的研究与应用.pdfVIP

武钢板坯连铸中间包自动开浇技术的研究与应用 1 2 1 1 1 王延锋 杨治争 饶江平 孙云虎 杨东明 （1.武钢炼钢总厂四分厂，武汉 430083 ；2. 武钢研究院，武汉 430081 ） 摘 要 本文以武钢炼钢总厂四分厂连铸车间现有设备为基础，介绍了中间包塞棒控流条件下的自动开浇工艺过 程、拉矫机启动控制、结晶器液位自动控制等内容，突出了结晶器液位控制在自动开浇过程中的决定性作用。实际 生产中，通过试验不断解决自动开浇中遇到的问题，使该厂的自动开浇率从开始时的月均 39%左右提高到当前 98% 以上的稳定状态。 关键词 塞棒 液位 控制系统 自动开浇率 Research and Development of Tundish Auto-casting Technology on Slab Casters of WISCO Wang Yanfeng1 Yang Zhizheng2 Rao Jiangping1 Sun Yunhu1 Yang Dongming1 th (1. 4 Sub-factory of General Steelmaking Factory of WISCO, Wuhan ，430083; 2. RD WISCO, Wuhan, 430081) Abstract Based on the equipment of continuous casting plant of the 4th sub-factory of general steelmaking factory of WISCO, the technology process of auto-casting, withdrawal straightening stands start-up controlling and liquid level of mould controlling were introduced at the condition of stopper controlling system, the critical function of mould level controlling was emphasized as soon.Through repetitive test and application, several problems were solved in industrial producing process, which promote the rate of auto-casting of that factory to beyond 98 percent stably from 39 at the beginning. Key words stopper, liquid level of mould, controlling system, auto-casting rate 1 引言 连铸中间包自动开浇是由 PLC 自动控制塞棒的开闭度和拉矫机的拉速实现全自动浇钢。该过程主要包 括钢包开浇后钢水注入中间包、中间包钢水自动浇注进结晶器及钢水在结晶器中到达设定的液面高度时, 铸 机自动起步、升速, 直至设定的目标拉速和目标结晶器液位两个过程，这两个过程是可以独立运行也可以联 动的。自动开浇的核心是根据钢种、断面控制好起步时间、起步拉速，保证结晶器钢水液面稳定，形成均匀 的坯壳。应用自动开浇技术可以防止操作不当造成开浇漏钢，提高开浇成功率。同时在保证钢水连续填充的 条件下，避免或减少铸坯的重接痕等缺陷。自动开浇技