结晶器保护渣对镀锡板表面质量影响分析.pdfVIP

1结晶器保护渣对镀锡板表面质量影响分析 陈志平 江中块 倪修华 （宝钢股份上海梅山钢铁有限公司，南京 210039 ） 摘 要 针对镀锡板存在表面质量缺陷的情况，研究分析了板坯连铸机用低碳保护渣特性。目前生产使用的保护渣各 项性能配合基本合理，满足生产要求，如能针对不同保护渣，控制合理的熔点和碱度，适当提高黏度，将利于均匀润 滑，减轻振痕深度，提高铸坯质量；基于对现用保护渣性能及使用状况分析，提出了保护渣的物性参数改进方向。 关键词 保护渣 连铸板坯 表面质量 Analysis on the Influences of Mould Flux on Tinplate Surface Chen Zhiping Jiang Zhongkuai Ni Xiuhua (Baosteel Meishan Iron Steel Co.,Ltd., Nanjing,210039) Abstract At present,the tinplate features poor surface quality,thus the characteristics of mould flux for low carbon steel continuous casting.All the characteristics of the mould flux that using in Baosteel Meishan are basically reasonable and can satisfy the request of production.If the melting point and the alkalinity of the mold powder is right ,and improve the viscosity of mold powder appropriatly,the friction will be even,the depth of oscillation mark will become flatter, and the surface quality of casting slabs will be improved.The improving direction of properties of mold powders is brought forward based on the analysis of characteristics of mould powders and using state. Key words mold powder, continuous casting slab, surface quality 1 引言 上海梅山钢铁股份有限公司 2 号大板坯连铸机，2003 年初投产，铸机原为一机一流，2008 年，对该铸 机进行改造，新增一流变成二机二流。铸机冶金长度 41.3m，产品规格：厚210 mm 宽 900～1320 mm。该 铸机装备：结晶器内置电磁制动、结晶器液压振动、二冷段气雾冷却、铸机水平段的轻压下技术、漏钢预报 技术等。随着铸机生产品种越来越多样化，部分钢种（如 MRT-4 等）出现了较严重的质量问题，主要是热 轧板的边部出现“翘皮”缺陷，封锁率严重。为此，梅钢就 MRT-4 热轧板“翘皮”缺陷控制展开专题研究， 其中保护渣对于连铸坯表面质量有重要影响，是专题研究的重点内容。 2 保护渣性能优化研究 根据课题研究内容，在对国内相关钢厂大板坯连铸调研的基础上，结合 MRT-4 钢连铸的工艺特点，对 连铸现用保护渣给出了技术分析和评价，并在此基础上提出改进建议。 2.1 MRT-4 钢的特性及对保护渣要求 根据 MRT-4 钢的具体成分，可知该钢种碳含量处于中碳包晶钢范畴，属裂纹敏感钢种。由于钢的特性 陈志平，男，博士，高级工程师，6713910@ 结晶器保护渣对镀锡板表面质量影响分析 8-607 （钢的性能、凝固特性）、坯型和浇注工艺是选择保护渣性能的主要依据。此处主要从