管线钢连铸轻压下工艺的研究.pdfVIP

管线钢连铸轻压下工艺的研究 任子平 孙 群 （鞍山钢铁集团公司，鞍山 114021 ） 摘 要 鞍钢 ASP 铸机均采用奥钢联 SMART 扇形段并配有动态轻压下技术。为了充分发挥该铸机动态轻压下技 术在提升铸坯内部质量方面的作用，本文进行了应用管线钢连铸轻压下技术的试验研究。通过分析中心偏析的形成 机理，研究连铸轻压下工艺的设计原则。利用枝晶检验和化学成分分析等手段，研究不同轻压下位置对于连铸坯中 C、Mn、P 元素偏析的影响作用，从而对现行的动态轻压下位置进行了优化调整，进一步提高了管线钢连铸坯的内 部质量。 关键词 管线钢 轻压下 中心偏析 Study on Soft Reduction Technology of Pipeline Steel Continuous Casting Ren Ziping Sun Qun （Anshan Iron Steel Co.,Ltd., Anshan, 114021 ） Abstract The ASP continuous caster used in AISC was all equipped with VAI SMART sector section as well as dynamic soft reduction techniques. In order to sufficiently play the role of this certain continuous caster’s effect on enhancing the inner quality of casting billet, experimentally study towards dynamic soft reduction of pipeline steel casting was adopted in this paper. The design principle was studied by analyzing the formulation mechanism of central segregation. With dendrite test and chemical analysis, the effect of element segregation of carbon, manganese and phosphor at different soft reduction position was studied. By all these, the current dynamic soft reduction position was optimized, which would enhance the inner quality of casting billet of pipeline steel. Key words pipeline steel, soft reduction, central segragation 1 引言 连铸轻压下是指在铸坯凝固末端一个合适的两相区内利用当地的夹辊或其他专门设备，对铸坯在线实施 一个合适的压下量，用以抵消铸坯凝固末端的体积收缩，从而抑制因凝固收缩引起的浓化钢水的流动与积聚， 减轻中心宏观偏析程度的铸坯凝固过程压力加工技术[1～3] 。其中，将只能在铸机辊列某一固定位置实施的轻 压下称之为静态轻压下[4] ；能够在线跟踪铸坯的热状态，并根据当时的实际凝固位置实施轻压下称之为动态 轻压下[5] 。动态轻压下是当前国际上正在大力发展的连铸新技术，由于其在提升铸坯内质、提高连铸效益等 方面独特的优越性，已得到国内外日益广泛的重视。 诸多研究表明[6,7]，轻压下技术对改善铸坯的中心偏析有着显著的作用，因此为尽可能降低管线钢连铸 坯中心线偏析的严重程度，目前鞍钢 ASP 铸机采用奥钢联 SMART 扇形段并配有动态轻压下技术。为了充 分发挥该铸机动态轻压下技术在提升铸坯内部质量方面的作用，研究降低管线钢连铸坯中心偏析技术和轻压 下的技术有着极其重要的作用