动态配水在宣钢150炉区1号方坯连铸机中的应用.pdfVIP

1 动态配水在宣钢 150 炉区 1 号方坯连铸机中的应用 王剑锋 郝 忠 （宣钢炼钢厂，宣化 075100 ） 摘 要 在坯龄模型基础上，根据计算出的铸坯表面温度与目标温度的差值进行优化调节水量。设计了宣钢 150t1 号方坯连铸机二冷动态配水模型实现铸坯表面温度自适应控制。该模型使二次冷却更加均匀，减少了铸坯表面回温， 以便达到控制铸坯组织和内部质量的目的。 关键词 连铸 动态配水 表面温度 二冷 Application of Dynamic Water Distribution in the Xuanhua Steel No.1 Continuous Casting of Steel Slab Wang Jianfeng Hao Zhong (Steelmaking, Xuanhua Iron and Steel Group Co., Ltd., Xuanhua, 075100) Abstract Based on the slab age control model ．The difference between surface temperature of the slab and the target temperature is used to optimize the control of the secondary cooling ，and the cooling model is designed to achieve slab surface temperature self adapting control system of XUANGANG No．1 slab continuous casting machine．This model can make secondary cooling more evenly and reduce the slab back to the surface temperature in order to achieve control and internal slab quality ． Key words continuous casting, dynamic water distribution, surface temperature, secondary cooling 1 引言 二冷配水是决定铸坯内部质量的重要因素，对于工艺条件频繁变动的连铸生产现场，只有实现了优质的 动态配水，才能保持合适的目标温度和稳定的铸坯表面温度，从而减小铸坯自身的热应力和机械应力，保证、 提高铸坯质量，保护铸机。另一方面，动态配水的实现也是应用先进冶金技术（如凝固末端电磁搅拌、动态 轻压下等），以及质量分析的基础。 目前先进的连铸配水控制方法就是根据坯龄(凝固历程，坯壳生成后所经历的时间)模型，将各个冷却段 的计算温度和目标表面温度相比较，根据温差计算调整后的冷却水量，并进行控制。在完善宣钢 150t1 号连 铸机项目中，通过增加二级动态配水系统，将原来的以拉速为控制参数改为以坯龄为控制参数，改变了原有 的配水模式。实践证明，1#方坯连铸机在逐步适应二冷动态配水的过程中，铸坯表面、内部质量都得到了较 大的提高。 王剑锋，炼钢工程师，zhaoguoying723@ 8-488 第八届（2011 ）中国钢铁年会论文集 2 工艺概况 表1 宣钢150t1 号方坯连铸机基本参数 铸机类型 全弧型 铸机半径/m 10 流数/流 12 铸