amdac的反相乳液聚合及絮凝性能评价word格式论文.docxVIP

摘要论文采用反相乳液聚合法，以丙烯酰胺(AM)和丙烯酰氧乙基三甲基氯化铵 (DAC)作为单体，Span80-Tween80 为复合乳化剂，液体石蜡为连续相制备污泥脱 水剂阳离子型聚丙烯酰胺（CPAM）。实验考察了油水体积比、乳化剂用量和配比、 单体用量和配比、引发剂种类和用量、温度、聚合时间、通氮气时间和搅拌对聚 合物特性黏度和稳定性的影响。研究结果表明：在油水体积比为 1:1.6、乳化剂用 量为 30%（占液体石蜡的质量分数）、乳化剂 Span80 与 Tween80 质量比为 3:5、单 体用量为 30％（占水相质量分数）、单体 AM 与 DAC 摩尔比为 2:3、引发剂用量 为 0.15％（占单体的质量分数）、聚合温度为 40℃，通入普通氮气 30min，聚合时 间为 5h 的条件下，得到特性黏度为 897 mL·g-1，阳离子度为 60%的阳离子聚丙 烯酰胺。对制得的产品进行脱乳和干燥，干燥的优化条件是在真空度为 1000Pa，温度 为 60℃～70℃范围内干燥 10h 左右，所得产物效果较好。通过红外光谱和差热分 析对自制的 CPAM 进行了结构表征。结果显示：通过红外光谱分析证明自制的 CPAM 结构与理论产物结构相符，通过差热分析内表明自制 CPAM 在 265.54℃时 发生化学分解。将自制的阳离子聚丙烯酰胺用于重庆市鸡冠石污水处理厂浓缩池的污泥处 理，实验研究表明阳离子聚丙烯酰胺用于污泥脱水，其脱水效果与阳离子聚丙烯 酰胺的特性黏度、阳离子度、投加量和搅拌速度等因素有关。在阳离子聚丙烯酰 胺特性黏度为897 mL·g－1，质量分数为0.05‰，投加量为25mL的情况下进行絮凝实 验研究结果表明：污泥的透光率可达96.9％，滤液浊度可达11.2，滤饼含水率可达 62.05％。此外，论文还研究了阳离子聚丙烯酰胺的特性黏度、投加量、阳离子度 对污泥脱水效果的影响。研究结果表明：就目前实验室制备的阳离子聚丙烯酰胺 的情况下，投加量和阳离子度对污泥脱水效果的影响有一个最佳范围，特性黏度 越高絮凝性能越好，但是这仅限于目前实验室合成产物的特性黏度。除此之外， 温度，搅拌速度等也对污泥脱水有一定的影响。关键词：阳离子聚丙烯酰胺，反相乳液聚合；丙烯酰氧乙基三甲基氯化铵，丙烯 酰胺，污泥脱水ABSTRACTThe cationic polyacrylamide (CPAM) was synthesized by inverse emulsion polymerization using acrylamide (AM) and acryloyloxyethyltrimethyl ammonium chloride (DAC) as monomers, Span80-Tween80 as compound emulsifier, liquid paraffin as continuous phase. The influences factors to the viscosity of product and the stability of the system were discussed, such as the volume ratio of oil to water, the ratio and concentration of Span80 to Tween80, the ratio and concentration of AM to DAC, the type and concentration of initiator, the initial reaction temperature, reaction time, inlet time of N2, whisk speed, the drying and granulation. The optimum conditions ofcopolymerization were obtained as follows：the volume ratio of oil to water was 1:1.6,the emulsifier dosage was 30%, the mass ratio of Span80 to Tween80 was 3:5, the concentration of monomer was 30%, the mol distribution ratio of AM to DAC was 2:3,initiating temperature was 40℃, inlet time of N2 was 30min and reaction time was 5hours. The cationic polyacryla