厚度300mmS355J2+N欧标结构钢板正火工艺研究.pdfVIP

第37卷第2期 江 西 冶 金 Vol.37, No.2 2017 年4 月 JIANGXI METALLURGY April 2017 　 　 文章编号:1006-2777(2017)02-0005-03 厚度300 mm S355J2 +N欧标结构钢板正火工艺研究 刘坚锋,王琨铭 (新余钢铁集团有限公司,江西 新余　 338001) 摘 要:　 对300 mm S355J2+N欧标结构钢进行了不同温度的正火试验,观察其显微组织并分析了不同条件下钢 板的力学性能,结果表明:880 ℃正火,可以得到更好的低温韧性,随着保温时间的延长,钢板组织晶粒越大。 关 键 词:　 特厚板;正火;组织;性能 + 中图分类号:　 TG335.5 1;TG156.4 文献标志码:　 A Study on Normalizing Technology of Steel Plates GRD. S355J2 + N with Thickness300mm Liu Jianfeng,Wang Kunming (Xinyu Iron Steel Group Co. ,Ltd. Xinyu338001Jiangxi,China) Abstract:　 The normalizing experimentesfor steel S355J2+Nwiththickness300mmarecarriedout at differenttemperatures. The microstructures of the steel are observed and the mechanical properties of the steel plate under different conditions are analyzed. The results show that the better toughness can be obtained by normalizing at 880 DEG C,and the grain size is getting larger with the holding time is lasting. Key words:　 extra-thick plate;normalization;construction;performance 理的正火工艺。 0　 前言 1　 试验材料及试验方案 钢板一般按厚度分为中厚板(4 ~20 mm)、厚板 (20~60 mm)和特厚板(大于60 mm)。 随着国民经 1.1　 材料 济的快速发展,特厚板的市场需求日趋旺盛。 为满 采用420 mm 连铸机生产的断面为420 mm 的 足市场需求,新钢基于420 mm 特厚板坯连铸生产 坯料,其化学成分见表 1。 坯料经车底式加热炉加 线,开发出了厚度不大于300 mm S355J2+N低合金 热,均热温度 1 200 ~ 1 250 ℃,在炉时间 8．5 ~ 结构板,但厚度为200 ~300 mm 的钢板 -20℃冲击 9．5 h,开轧温度大于1050 ℃,经除鳞后采用高温再 性能合格率较低。 为解决这一问题,对300 mm 厚 结晶轧制,终轧温度大于 1 000 ℃,轧制成厚度 S355J2+N钢板正火工艺进行试