铸铁型下料口水套的工艺设计.pdfVIP

学兔兔 铸铁型下料口水套的工艺设计 何伟荣 (上海宝钢铸造有限公司，上海201900) 摘要：为解决钢结构型下料口水套使用中存在的问题，设计了铸铁型下料口水套的结构，分析 了其设计要求，制定了冷却管弯制工艺和铸件本体铸造工艺，最终研制出铸铁型下料口水套。 使用结果表明，铸铁型下料口水套具有整体刚性强，耐热、耐磨，导热性能好等优点，避免了 炉料对冷却管的磨损和冲击，延长了使用寿命。 关键词：铸铁型下料口水套；铸造工艺；结构设计 中图分类号：TG255 文献标识码：A 文章编号：1 673—3320(2014)02—0013—03 Process Design of Cast Iron Water Jacket for Discharge Outlet HE Weirong (Shanghai Baosteel Casting Co．，Ltd．，Shanghai 201900，China) Abstract：To solve the problems existing in use of the steel water jacket for discharge outlet，the structure of cast iron water jacket for discharge outlet was designed．Its design requirements were analyzed．The bending process of cooling pipe and the casting process ofjacket body were established．Finally the cast iron water jacket for discharge outlet was developed．The application results show that the cast iron water jacket for discharge outlet has the advantages of stronger rigidity,heat resisting and wear resisting and be~er thermal conductivity．The abrasion and impact of furnace charges to cooling pipes are avoided to prolong the service life． Key words：cast iron water jacket for discharge outlet；casting process；structural design 下料口水套是炼钢转炉或混铁炉的加料 示。这种结构由于受热应力频繁变化，致使焊缝 部位，其工况十分恶劣，一方面受到高温钢水 应力过大，易开裂漏水；此外，受热管在炉料的 1000 oC左右的热辐射作用，另一方面受到炉料 冲击及摩擦下，易磨损破裂，导致漏水。 的摩擦及撞击。在这些热应力和机械应力的综 合作用下，传统的钢结构型下料口水套经常出 现变形、开裂、漏水等现象。这种下料口水套不 但使用寿命短、维护困难，而且给生产带来安全 隐患。为延长下料口水套使用寿命及保证其安全 性，提高生产效率，研制一种耐高温、抗冲击的 下料口水套具有重要意义。 1 下料口水套结构设计 钢结构型下料口水套通常由上法兰、上联 图1 钢结构型下料口水套 箱、受热管、下联箱、进水联箱、面板组成。这 为解决钢结构型下料口水套使用中存在的问 些结构通过焊接方式连接成下料口水套，如图l所 题，设计了一种铸铁型下料口水套，如图2所