铸态QT700-10技术初探.pdf

学兔兔 May2014 VOI．63 NO．5 铸态QT700—1 O技术初探 柳建国 ，曾大新 (1．东风精密铸造有限公司，湖北十堰442714；2．湖北汽车工业学院，湖北十堰442002) 摘要：近年有关高强度、高伸长率球墨铸铁的研究与生产技术开发受到相关研究机构的关注。通过采用合理的成分 设计、铁液净化、多元素合金固溶强化、晶粒细化等一系列生产工艺措施，探讨了铸态QT700．1032艺开发的可行性。 关键词：铸态球铁；化学成分；力学性能 中图分类号：TG143．5 文献标识码：A 文章编号：1001—4977(2014)05—0507—03 PreIiminary Discussion on Technology of Ductile Iron of As．Cast QT700．1 0 LIU Jian—guo ，ZENG Da—xin (1．Dong~ng Investment Casting Co．，Ltd．，Shiyan 442714，Hubei，China；2．Hubei University ofAutomotive Technology，Shiyan 442002，Hubei，China) Bd 暖辑 Abstract： In recent years， study on the ductile iron with high strength and high elongation and the development ofproduction technology received attention ofrelated research institutions．Through experiment， the feasibility of developing as—cast QT700-10 technology was discussed by using a series of production processes such as reasonable composition design，molten iron purification,multi—element alloy solid solution strengthening，grain refinement,etc． Key words：as—cast ductile iron；chemical composition；mechanica1 properties 随着汽车工业的进步，商用车、重卡朝着重载、 分及性能进行解读 ，SiboDur球墨铸铁形成了 高速、低耗、低成本及良好的舒适性等方向发展，汽 SiboDur450—17、 SiboDur550—12、 SiboDur700—10、 车底盘支架、托臂梁等零部件对高强度、高伸长率材 SiboDur800—5系列，力学性能指标在传统球墨铸铁力 料的综合性能要求也越来越高 就材料的综合性能和 学性指标中分布见图1。 成本而言，高强度、高伸长率球墨铸铁备受青睐，目 前国家标准中关于球墨铸铁的要求，一般是低强度高 伸长率或是高强度低伸长率，对于那些不仅要求高强 度、还要求高韧性、高疲劳性能等的铸件，传统国标 的球墨铸铁材料不能满足性能要求。因此我公司与湖 北汽车工业学院联合开展了高强度、高伸长率球墨铸 铁研究工作，以满足汽车零部件轻量化需求。 1 国内外球墨铸铁发展现状 目前球墨铸铁的生产，都是根据GB／T 1348--2009 墨铸铁件》标准，球墨铸铁的力学性能从QT350—