沙柳树皮板制造及工艺优化 贺勤 王喜明 (内蒙古农业大学材料科学与艺术设计学院，内蒙古呼和浩特，010018) 摘要：本研究主要探讨利用脲醛树脂胶制造沙柳树皮板可行性，并且利用均匀设计和回归分 析法对沙柳树皮板的工艺进行优化设计。结果证明，沙柳树皮板的性能与其它树皮板材的接 2 近，通过逐步回归分析，建立因素和指标的拟合方程，二次方程较一次方程要好些，且 R 值均在 0.9300 以上。利用拟合方程得到最佳工艺参数为：刨花尺寸孔径为 10.96mm、施胶 量为 14％、闭合时间为 3s、热压温度为 160℃、热压时间为 460s。 关键词：沙柳 树皮板 均匀设计 回归分析  Optimization Study on Processing of Salix Barkboard  Abstract: The objective of this study was to determine the technical feasibility of making particleboards from  Salix bark residues bonded with urea formaldehyde resin and to use uniform design and regression analysis  algorithms to optimize the technical parameters. It was improved that the properties of particleboards from Salix  bark residues is  similar with the particleboard by   bark, the multi linear regression  equation used stepwise  2  regression analysis is better than unitary linear equation, and R  is above 0.9300. Base on the study the optimum  conditions is bark residues size:10.96mm,resin content:14%, close time:3s, temperature:160 ℃ and time:460s.  Key words:Salix   Bark board  Uniform Design   Regression Analysis  近几年我国人造板在以每年 20%的增长率发展，据不完全统计，2004 年人造板总产量达 5446.49 万立方米。然而森林资源远远不能适应这种需求，于是森林废料、木材加工剩余物 以及农作物剩余物这些数量庞大的原料越来越引起人们重视。 沙柳是西北地区一种最主要的 人造板用材，上世纪 90 年代以来，几家以沙柳为原料的生产企业在鄂尔多斯市陆续投产， 年加工生产刨花板和中密度板 10 万多平方米，消耗沙柳 14 万吨左右。而沙柳的树皮含量很 [1] 高，体积百分比约为 25.4％ ，如何合理有效的利用这部分资源具有很高的现实意义。 经过研究者几十年的研究证明，制造树皮板是可行的。总体来看，树皮板的力学性能要 低于木质人造板的，为了解决这一问题，研究者多数选择在树皮板中加入木质原料以提高板 [2][3] 的力学性能。 但是树皮板绝缘性提高，热导率降低，甲醛释放量降低，而且还有抗腐朽， [4][5][6][7] 抗真菌和阻燃的优越性能,可做地板、天花板、隔板等建筑材料以及装饰树皮板。 树 皮板的