中国胶粘剂990511 中国胶粘剂 CHINA ADHESIVES 1999年 第8卷 第5期 Vol.8 No.5 1999 增粘树脂对聚丙烯酸酯压敏胶粘合性能的影响 李明　徐秀雯　李琴　陶学娣 　　【摘要】　　聚丙烯酸酯乳液和增粘树脂松香、C 5石油树脂乳液共混，用共混液 涂布成压敏胶带。考察了不同增粘树脂用量对压敏胶带粘合性能的影响。结果表明， 随松香树脂量增加，180℃剥离强度提高，并出现峰值；快粘力不变；持粘力下降。随 C 5石油树脂量增加，180°剥离强度，快粘力，持粘力均大幅度下降。 　　关键词：压敏胶　聚丙烯酸酯乳液　增粘树脂乳液 The Influence of Tackifier Resins on the Adhesion of Polyacrylate Pressure-Sensitive Adhesive Li Ming　Xu Xiuven　Li Qin　Tao Xuedi (Suzhou Univercity) 　　Abstract　Polyacrylate emulsion was blended with tackifier resin such as rosin emulsion, C5 petroleum resin emulsion. The influence of the content of tackifier resin on the adhesion properties of polyacrylate was investigted. The results show that the 180° peel strength increases and come to a peak value, the ball tack is not change and the hold tack decreases as the amount of rosin increases. For C5 petroluem resin the 180° peel strength, ball tack and hold tack all decreases as it in creases. 　　Keywords: Pressue sensitive adhesive　Polyacrylate emulsion　tackifier resin emulsion 前言 　　压敏胶及其制品因使用方便，发展很快。按压敏胶所使用的胶粘剂种类，可分为 橡胶类和聚丙烯酸酯类压敏胶。橡胶类一般都需要加入增粘树脂。而聚丙烯酸酯类由 于其可以通过调节单体种类和用量来控制粘合性能，一般都不添加增粘树脂。近来， 为了提高压敏胶的性能，特别是对聚乙烯、聚丙烯等难粘材料的粘合性，降低压敏胶 ［1］［2］ 成本，有人开始研究在聚丙烯酸酯类添加增粘树脂 。本文用松香和C 石油树 5 脂作为增粘树脂，添加到聚丙烯酸酯乳液中，制成压敏胶带，考察了增粘树脂的用量 对胶带的快粘力，180°剥离强度和持粘力的影响。 万方数据 file:///E|/qk/zgjnj/zgjn99/zgjn9905/990511.htm（第 1／6 页）2010-3-23 15:17:25 中国胶粘剂990511 1　实验 1.1　原料 　　聚丙烯酸酯乳液由上海丙烯酸厂提供，可直接用于涂布压敏胶带。C 5石油树脂由 美国的EASTMAN Co.提供。松香、乳化剂、保护胶体，pH调节剂等由市场购得。 1.2　增粘树脂乳液配制 　　C 石油树脂流动温度为120℃，难于用常规分散法配成水乳液。按C树脂∶液体石 5 5 蜡＝100∶1