邯宝炼钢厂 250t 包烘烤研究 1 1 1 1 1 2 潘树敏 张征辉 严向奇 李斌 艾晓礼 程迪 （1.河北钢铁集团邯钢邯宝炼钢厂；2.河北钢铁集团邯钢技术中心，邯郸 056015 ） 摘 要 为解决河北钢铁公司邯宝炼钢厂 250T 钢包在新包烘烤过程中出现的耐材开裂、崩料等问题，通过测量 钢包烘烤过程中钢包耐材各部位的温度变化，确定目前钢包烘烤模式的弊端；并通过数字模拟钢包烘烤过程，结 合实际运行效果，探讨最优化的钢包烘烤方案。 关键词 铝镁碳钢包 预制块钢包 热电偶 数字模拟 烘烤模式 250 t Ladle Thermal State of Baking Pan Shumin1 Zhang Zhenghui1 Yan Xiangqi1 Li Bin1 Ai Xiaoli1 ChengDi2 1. Hebei Handan Iron Steel Group Bao Steel Plant Handan Iron Steel; 2. Hebei Handan Iron Steel Technological Center, Handan, 056015 Abstract To address Bao Steel Plant Handan, Hebei Iron and Steel Company in the new package 250T Ladle occurred during baking Refractories cracking, collapsing materials and other issues, by measuring the ladle ladle refractory curing process the temperature change of each part, find the current ladle drying Grilled drawbacks of the model; and Ladle through digital simulation process, combined with the actual operating results to find the most optimal Ladle program. Key words magnesium carbon package, preform ladle, thermocouple, digital simulation, baking mode 1 引言 邯宝公司炼钢厂配备三座 250t 转炉，两座 LF 精炼炉及一座 RH 精炼炉，两台 2150 两机两流板坯连铸 机，年钢产量在 500 万吨以上，其产品主要为管线钢、汽车用钢等高端品种钢。与其品种结构相配套的钢 包系统目前具有两种材质：一种为普通铝镁碳材质钢包，一种为预制块无碳钢包。 邯宝炼钢厂钢包在新包烘烤过程中，原来经常出现包底烤裂或工作层崩料等现象，严重制约钢包的运 行效率和成本的降低。为了找出原钢包烘烤模式所存在的弊端，并寻找最优化钢包烘烤模式，炼钢厂进行 了一系列试验，最终确定了适合的钢包烘烤模式。 2 钢包热状态研究思路 数据分析：现场温度测试试验→烘烤测试数据分析 数值模拟：钢包投入使用前热状态模拟→包内烟气燃烧温度场模拟→提出钢包烘烤优化方案。 3 钢包上线烘烤数据分析 3.1 热电偶的埋设 钢包热状态现场测试实验是通过在钢包内部埋设热电偶测试钢包各部位的温度变化过程，热电偶的具 体埋设位置见图 1 和表 1。 邯宝炼钢厂250t 包烘烤研究 8-571 钢包全修过程中进行热电偶埋设。修包完成后，对钢包烘烤以及冷却过程进行连续测试。新钢包的连 续测试包括：修包完成后烘烤过程、包底安装机构和维护时的钢包冷却过程、钢包投入使用前的再烘烤过 程。 图 1 热电偶埋设图 表 1 热电偶埋设的具体位置 热电偶编号 位置 备注 1 绝热层与包壳间 2 包壁渣线处 永久层与绝热层间 3 工作层与永久层间 4 绝热层与包壳间 5 包壁中部 永久层与绝热层间 6 工作层与永久层间 7 绝热层与包壳间 8 包壁底部 永久层与绝热层间 9 工作层与永久层间 10 绝热层与包壳间 11 包底 永久层与绝热层间 12 工作层与永久层间 13 包壁上渣线处 14 包壁中部 包衬内表面 15 包壁与包底交接处 16 包底中央 3.2 钢包上线时烘烤数据的分析 在邯宝炼钢厂，先后针对 23 号预制块钢包和 32 号铝镁碳钢包进行了现场跟踪测试。测试数据分析如 下。 8-572 第八届（2011 ）中国钢铁年会论文集 3.2.1 预制块包上线