99-04-铸造复合轧辊的几种新方法.PDFVIP

生产技术 特种铸造及有色合金　1999 年第 4 期 铸 造 复 合 轧 辊 的 几 种 新 方 法 北京冶金设备研究院　王贵明 摘　要　高速钢用作轧辊材料使冷、热带钢工作辊寿命得到大幅度提高, 但是用常规生产方法包括离心铸造法很难生产 出高速钢复合轧辊。介绍了几种新的复合轧辊的生产方法, 成功地生产出外层与心轴良好结合的高速钢复合轧辊, 其中一 些方法可方便地复合各种材料。 关键词: 复合轧辊　高速钢　电渣重熔　连续浇注　喷射 Severa l New W ays for Ca sting Com pound Rolls W ang Guim ing (Be ij ing M eta llug ica l Equipm en t Research In stitute) ABSTRACT　T he h igh speed steel as a ro ll m aterial sign ifican tly increased the service life of ho t and . co ld strip m ill w o rk ro lls Bu t it is very difficu lt to p roduce the H SS com pound ro lls by conven tional m ethods including cen trifugal casting. Several new w ays fo r m ak ing H SS com pound ro lls are in troduced. By tho se m ethods H SS com pound ro lls are m anufactu red w ith good bonding at the in terface of the co re . cladding alloys O f the m ethods the m aterials w ith very differen t chem ical com po sition can be conven ien t ly cladded on the co re alloy. Key W ords: Com pound Roll, H igh Speed Steel (HSS) , Electroslag Rem elting, Con tinuous Csa ting, Spary 　　90 年代开发的高速钢复合轧辊在冷、热带钢轧机 固的外层高速钢的内表面熔融混合。这一熔融层的熔点 上作为工作辊, 使用期限成倍增加, 正在获得广泛应用。 比心部钢液低, 成为最后凝固的部位, 极易产生铸造缺 ( ) 这种高速钢复合轧辊的外层是高碳高速钢 用于热轧 陷、降低结合部位的强度。当要求心部材料选用锻钢时, ( ) 和半高速钢 用于冷轧 而心部是高强度的铸钢或锻钢, 离心铸造法更无法做到。 [ 1 ] 用原先的铸造复合轧辊的方法 , 包括离心铸造方法难 1. 2　解决途径 以制造, 因而相继开发出一些新的复合轧辊的铸造方