卷取机缠上夹送辊事故原因分析与措施.pdfVIP

卷取机缠上夹送辊事故原因分析与措施 赵艳良 杨付勇 王春生 田吉祥 （河北钢铁集团邯钢公司，邯钢连铸连轧厂，邯郸 056003 ） 1 摘 要 邯钢 CSP 卷取机出现带钢缠上夹送辊事故，严重制约了生产的正常进行，分厂组织各专业的技术人员对 此项事故进行专题分析并采取必要措施遏制事故的发生；通过采用的各种办法以及观察其使用效果，经过总结、分 析、整理后归纳出分析带钢缠上夹送辊事故的方法，并且为以后生产中避免此类事故的发生积累了一定的经验和措 施。 关键词 夹送辊 事故分析 措施 The Reason Analysis and Measure of Tie Up to Pinch Roll Zhao Yanliang Yang Fuyong Wang Chunsheng Tian jixiang (CSP Plants, Handan Iron and Steel Company, Hebei Iron and Steel Group，Handan, 056003 ) Abstract The Han steel CSP takes machine to appear to take a steel to tie up to pinch roll trouble, Seriously influenced to produce normally to carry on, Divide the factory organizes each professional technical personnel to carry on analysis to the trouble, and adopt necessary measure to prevent from trouble of occurrence, Through summary, analyze to tally up to have an accident behind past of method, and is hereafter produce medium avoid trouble of occurrence backlog certain experience and measure. Key words pinch roll, trouble analysis, measure 1 引言 邯钢 CSP 生产线投产以来，时常会出现轧制薄规格时带头缠到上夹送辊的事故。由于以前带卷缠上夹 送辊次数比较少，处理比较及时，没有引起足够的重视。由于缠夹送辊事故的出现严重制约生产，解决带钢 缠上夹送辊这个问题就显得尤为重要，本文详细地将缠上夹送辊要考虑的几个方面进行分析、总结，提供一 个思路，为以后的生产管理打下一个良好的基础。 2 缠上夹送辊事故案例的现象分析 2.1 事故报告 某年 9 月 14 日9：17，1 号卷取机在卷取 2.0mm 带钢时，带头未进入卷取机，操作工发现后，迅速拍 下辊道快停和 1 号卷取机快停，发现带头缠绕在 1 号卷取机上夹送辊上（上夹送辊上缠绕了 6 圈带钢）。 2.2 缠上夹送辊事故的分析方向 在夹送辊控制中，上下辊转速比、偏移量、卷取厚度、夹送辊压下量、夹送辊磨损、夹送辊冷却水和轧 件材质对带钢头部弯曲影响很大。在这些因素的影响下，任何一种因素发生变化都可能会导致带钢头部向上 赵艳良，男，本科，工程师，金属压力加工，xiaoerzyl@ 邯钢无取向电工钢夹杂物演变分析 8-23 方或向下方发生弯曲，上下辊转速比对轧件头部弯曲的影响曲线呈波浪形状，规律很复杂。分析缠上夹送辊 事故就是要使带头向下弯曲而不是向上弯曲。 3 分析带钢缠上夹送辊事故的原因及措施 为了分析带钢缠上夹送辊的原因，从工艺、设备、电气控制等方面来分析，并查找出问题的原因并采取 了一些措施。 3.1 人为因素 首先查找