马钢环保自润滑热浸镀锌产品的开发.pdfVIP

马钢环保自润滑热浸镀锌产品的开发 杨兴亮 赵云龙 崔 磊 （马鞍山钢铁股份有限公司技术中心） 1 摘 要 本文介绍了马钢环保自润滑热浸镀锌钢板的开发、试制情况，并通过高速深冲实验、盐雾实验、涂装实验 比对普通热浸镀锌钢板和自润滑热浸镀锌钢板的各项工艺性能指标，得到了优化的系统工艺，成功开发了马钢环保 自润滑热浸镀锌产品，并在IT 制造、微电机制造领域得到应用。 关键词 自润滑热浸镀锌钢板 环保 Development of Hot-dip Galvanized Product with Self-lubricating Passivation Coating Yang Xingliang Zhao Yunlong Cui Lei (Technology Center, Maanshan Iron Steel Co., Ltd.) Abstract this paper introduces the development and production of self-lubricating Galvanized steel sheet in Masteel. The comparison of material property between self-lubricating galvanized steel sheet and traditional galvanized steel sheet have been evaluated and studied by salt spray test, cup drawing test and painting test. On this basis, the technology parameters have been optimized, and self-lubricating galvanized steel sheet has been successful developed. Now, it is widely applied to IT and micro electric motor, etc.. Key words self-lubricating passivation, hot-dip galvanized steel sheet, environment protection 1 引言 镀锌钢板由于其耐蚀性能、涂装性能良好，在家电产品、视听及办公用品中有着广泛的应用，但由于镀 层表面较软，与模具之间的摩擦系数较高导致其成型性能较差。因而镀锌钢板在成型加工中为防止开裂，一 般在其表面涂覆润滑油，提高其成型性能，成型加工完成后使用脱脂剂除去工件表面的油渍。然而涂覆润滑 油又带来一系列的问题：增加了涂油和脱脂工序，工艺流程繁杂；涂油过程恶化工作环境；脱脂过程使用含 有三氯乙烷和氟利昂等对臭氧层具有破坏作用的脱脂剂，破坏臭氧层；复杂成型条件下，即使涂有润滑油， 工件表面仍然容易产生擦伤，恶化表面质量与耐蚀性能。同时，传统的涂油冲压工艺流程为：清洗钢板表面 防锈油→表面涂敷冲压润滑油→冲压加工→脱脂处理。流程较长，环节较多。基于此，为提高家电用镀锌钢 板成型性能，可以在无润滑油条件下成型加工，通过在镀锌钢板表面涂覆一层有机润滑膜，降低与模具之间 的摩擦系数，提高成型性能，加工行业可以避开流程中的较多的工艺环节，直接冲压成型，能够大大提高作 业效率。 热浸镀锌钢板的自润滑技术就是镀锌层通过与自润滑介质反应而在其表面形成具有自润滑能力皮膜的 过程。由于反应生成的自润滑膜和基体结合牢固，具有良好的冲压润滑性能，大量用于冲压变形较大的工件， 杨兴亮，男，硕士，高级工程师，主要从事热镀锌产品及工艺的研究，mgyxl@126.com 马钢环保自润滑热浸镀锌产品的开发 能大大提升工件的冲压变形性能及作业率。由于自润滑热浸镀锌钢板具有良好的润滑性，同时具备一定的电 绝缘性和耐蚀性，使其广泛应用于汽车、机械制造、家用电器等领域[1～5] 。而我国自润滑技术起步较晚，但 经过近几年的发展，国内极少数的钢铁企业仅在实验室进行研究自润滑技术，随着高档家电及机械制造业的 发展，其