转炉生产曲轴钢氮合金化工艺研究与实践.pdfVIP

1转炉生产曲轴钢氮合金化工艺研究与实践 钟晓丹 (本钢炼钢厂，本溪 117021) 摘 要 曲轴钢中含有一定量的氮可以改善钢材的力学性能。转炉生产曲轴钢成分控制关键是钢中氮的合金化。为 了使钢中氮达到标准要求含量，本钢采用转炉+LF+RH+矩形坯连铸工艺，通过 RH 全程用氮气做提升气体，同时 -6 -6 补加氮化锰合金，来满足钢中氮含量要求。通过实践，此工艺方法可行，氮含量可稳定控制在 120×10 ~160 ×10 。 -6 -6 在 RH 真空状态下，单纯通过氮气提升气体可以增氮 15×10 ~25 ×10 ；在提升气体为氮气的情况下，加入氮化锰 合金时氮的收得率为 15%~20%。 关键词 转炉 曲轴钢 氮合金化 Study and Practice of Nitrogen Alloying for Crankshaft Steel Produced by Converter Zhong Xiaodan (Steelmaking Plant,Benxi Iron Steel (Group) Co.,Ltd., Benxi, 117021) Abstract It improves mechanical property of crankshaft steel by adding certain quantity of nitrogen in molten steel. However the key control is nitrogen alloying of crankshaft steel produced by converter. By using nitrogen gas for lifting throughout RH process, and adding Mn N alloy, it can meet the requirement of nitrogen content in steel. It confirmed that 3 the method is feasible and steady by practice. At a status of vacuum, nitrogen gas lifting can increase nitrogen content 15 × -6 -6 10 ~25 ×10 . When using nitrogen gas for lifting, nitrogen yield is 15 to 20 percent. Key words converter, crankshaft steel, nitrogen alloying 非调质曲轴钢的生产一般通过在钢中加入一定量的氮来改善钢材的塑性和高温可加工性。转炉生产曲轴 钢由于采用铁水，钢中原始氮含量较低，必须在精炼工序氮合金化。本钢炼钢厂经过试验，采用转炉+LF+RH+ 矩形坯连铸工艺生产曲轴钢，通过 RH 提升气体改氮气，另外适当补充一定量的氮化锰合金来保证钢中的氮 含量。生产实践表明，通过此方法，可以稳定控制钢中的氮含量达到标准的要求。 1 生产现状 本钢最初生产曲轴钢时，为了保证钢中氮含量，LF 氮合金化，不走 RH 工艺。此工艺虽然能够保证钢 中氮的含量，但是由于该钢种合金量大，再