转炉冶炼低硅低温铁水的控制.pdfVIP

转炉冶炼低硅低温铁水的控制 梁祥远 齐志宇 辛国强 李 丹 （鞍钢第二炼钢厂，鞍山 114021 ） 1 摘 要 转炉冶炼低硅低温铁水由于渣量小、造渣难等原因，容易造成终点磷高。针对此现象，文章分析了冶炼中 期的（FeO ）、炉渣碱度、钢水温度对脱磷分配比的影响以及补炉第一炉对冶炼的影响。通过机理分析，结合倒炉 渣况和温度情况，从成渣途径、温度控制、炉渣碱度、枪位控制这几方面，对终点脱磷采取了相应的技术处理措施 及控制，取得了良好的冶金效果。 关键词 转炉 低硅铁水 低温铁水 脱磷 Smelting Control for Low Silicon and Low Temperature Molten Iron Liang Xiangyuan Qi Zhiyu Xin Guoqiang Li Dan (No.2 Steelmaking Plant of Anshan Iron and Steel Co.,Ltd., Anshan,114021) Abstract Smelts the low silicon low temperature molten iron in the converter easy lead to the end point phosphorus high,because of small slag quantity and alsgging hard etc.According to the phenomenon, this essay analyzes the influence of the smelting mid-term (FeO), slag alkalinity, molten steel temperature to the distribution ratio and the influence of the first heat steel of converter steelmaking after fettling to the smelting. Through the mechanism analysis, combining the condition of turning down and temperture, from the slag forming ways, temperature control, slag alkalinity, oxygen lance position control, we have taken the corresponding technical processing measure to the end point dephosphorization, has made the good metallurgy progress. Key words the converter, low silicon, low temperature, dephosphorization 转炉冶炼是一个复杂多变的过程，受铁水条件、废钢结构、造渣材料质量等多种因素的影响，钢水质量 差别很大，磷高是影响钢水质量的主要因素之一。目前，鞍钢第二炼钢厂南区转炉冶炼低硅低温铁水（[％ Si]0.2，T1230 ℃）占生产总量的 8%～10%，在冶炼过程中由于渣量小、造渣难，经常出现终点磷偏高或 超出标准的现象，反映在终点的渣况和温度上表现出了不同的特点。为了提高钢水质量，降低消耗，通过对 这种现象产生的机理进行分析，采取了有效的控制措施，取得了很好的效果。 1 生产概况 1.1 冶炼条件 鞍钢第二炼钢厂南区有三座百吨复吹转炉，其工艺参数见表 1，每炉钢水吹炼时间平均为 16min，日常 冶炼钢种以低碳铝镇静钢及低合金钢为主，工艺路线为：铁水预处理—转炉冶炼—LF 精炼—板坯连铸。 梁祥远，工程师，从事炼钢工艺的生产技术管理和研究工作。 8-720 第八届（2011 ）中国钢铁