模拟焊后热处理对S355J0钢性能及组织的影响.pdfVIP

模拟焊后热处理对 S355J0 钢性能及组织的影响 王勇 孙殿东 苏春霞 张起生 何毅 （鞍钢股份有限公司，鞍山 114001 ） 摘 要 分析正火及不同时间模拟焊后热处理对 S355J0 钢板力学性能及微观组织的影响，结果表明，该钢随着模 拟焊后热处理时间的增加，其强度及韧性均不同程度的下降，主要原因在于钢中第二相粒子的长大。而由于钢中仍 保留一定数量的第二相粒子，钢板在24h 的模拟焊后热处理后性能仍能够满足指标要求。 关键词 模拟焊后热处理 力学性能 微观组织 Effect of Simulated PWHT on Microstructure and Properties of S355J0 Steel Wang Yong Sun Diandong Su Chunxia Zhan Qisheng He Yi (Angang Steel Company Limited,Anshan,114001) Abstract Effects of normalizing and different holding time simulated PWHT on microstructure and properties of S355J0 steel were analyzed. The results show that with the holding time increased of simulated PWHT, both strength and ductility were fall down, the main reasons were growth of second precipitated phase. Due to some second precipitated phase always keep in the steel, the properties after simulated PWHT by 24 hours also could meet the challenge of standard. Key words simulated PWHT, properties, microstructure 随着国民经济的高速发展，国内重大专项工程、标志性建筑对高性能、高品质中厚板产品的需求与日俱 增，如：核电用钢、舰船用钢、锅炉压力容器用钢、工程机械用钢、管线用钢等专用钢板[1-3] 已供不应求。 并且不仅需求数量越来越多，质量要求也越来越高[4] 。其中对于核电用钢、锅炉压力容器用钢等的一项重要 检验要求就是要进行钢板模拟焊后热处理，以保证钢板焊接后的综合性能不会发生大的变化。 本文以65mm 厚S355J0 钢板为研究对象，重点研究了模拟焊后热处理前、后，不同时间模拟焊后热处 理对钢板组织、析出相、强度及韧性等方面的影响，为该钢种进一步拓展及应用提供数据参考。 1 试验材料及方法 试验材料为鞍钢生产的65mm 厚S355J0 钢板，主要化学成分（质量分数）为0.15%C、0.40%Si、1.55%Mn、 0.014%P、0.002%S 及（Nb+V+Ti ）≤0.08%，其余为Fe 。 钢板轧后进行正火处理，正火处理温度为900℃并保温一定时间，以保证实现奥氏体化。再从正火处理 后的钢板上取样进行模拟焊后热处理，模拟焊后热处理工艺分别为（1）保温温度600℃，保温时间12h；（2 ） 保温温度600℃，保温时间24h 。 从正火及模拟焊后热处理后的试板上（厚度1/4 处）截取拉伸、冲击、硬度及金相试样。拉伸采用φ10mm 标准圆拉伸试样并按GB/T228—2002 《金属材料室温拉伸试验方法》执行；冲击采用10mm×10mm×55mm 夏比V 型缺口冲击试样并按GB/T229—1994 《金属夏比缺口冲击试验方法》执行；钢板表面布氏硬度按 模拟焊后热处理对S355J0 钢性能及组织的影响 GB/T231—2002 标准《金属布氏硬度试验》执行；同时利用冲击试验余样为金相试样，经4%硝酸酒精溶液 腐蚀后，在光学显微镜下观察微观组织；最后采取复型方法，在Tecnai G2 20 透射电子显微