连退带钢头尾平整率波动及其对性能的影响 居发亮 刘贞伟 吴海飞 （宝钢股份，上海 200941 ） 摘 要 本文通过对宝钢3 条连退机组铝镇静钢和IF 钢带钢头尾部平整伸长率和力学性能检测的试验，发现了在带 钢头尾部平整率和力学性能存在较大波动，分析了平整率波动产生的原因和波动的形式，讨论了平整率对两者力学 性能的不同影响。 关键词 连退机组 平整 性能波动 钢带头尾 Temper-rolling Elongation Fluctuation and its Effect on Properties of the Head and Tail of CAPL Steel Strip Ju Faliang Liu Zhenwei Wu Haifei (Baosteel Co., Ltd., Shanghai, 200941) Abstract It was found that there is temper-rolling elongation fluctuation on steel strip head and tail through the research on CAPL steel strip temper-rolling efficiency and mechanical properties in this article. At the same time, why the temper-rolling efficiency fluctuates and what its style was studied. The effect on mechanical properties of temper-rolling elongation fluctuation on steel strip head and tail of AK steel and IF steel strip was also analyzed. Key words CAPL, temper-rolling elongation, properties fluctuation, head and tail of steel strip 1 引言 随着现代汽车工业的发展，用户对冷轧薄板的要求越来越高，市场竞争越来越激烈，罩式退火炉生产周 期长、表面清洁度低、性能均匀性差、成材率低等缺点显得越来越突出。连续退火机组集连续退火和平整工 艺为一体，具有生产效率高、表面质量好、性能稳定等优势，已逐步替代罩式炉，成为大型钢企生产汽车板 和家电用板的主要机组[1,2] 。由于是连续生产，所以前后带钢之间须通过焊接形成连续不断的带钢。平整工 艺为保证获得一定的平整伸长率，具有一定的轧制力和张力负荷，为保护焊缝，在焊缝过平整辊时，需要降 低轧制力，这可能会对带钢头尾力学性能造成影响。目前国外和国内对带钢整体性能研究的文献比较多，对 带钢头尾短距离性能的研究报道还很少。本文拟对普通铝镇静钢（AK 钢）和无间隙原子钢（IF 钢）带钢头 尾平整伸长率的波动情况和对带钢头尾性能的影响进行研究。 2 试验 本文以1.0mm 厚度AK 钢和IF 钢冷轧带钢为研究对象（成分见表1），经750～800°C 连续退火、伸长 率为 1.0%的平整轧制。为减小头尾热轧工艺波动带来的头尾性能差异，将30t 左右的大卷在冷轧轧机出口 分成3 个轧硬卷小卷，以中间小卷为研究对象。AK 钢和IF 钢分别选取3 个这样的小卷，分别在3 条不同 第八届（2011 ）中国钢铁年会论文集 的连退机组生产，AK 钢小卷编号为AK-A 号、AK-B 号、AK-C 号，IF 钢小卷编号为IF-A 号、IF-B 号、IF-C 号。后分别进行连续退火和平整，带钢退火温度波动控制在±5°C 内。通过平整机组平整率监测系统对带钢 头尾平整率进行记录，并最终考察6 个小卷的头尾性能情况，包括屈服强度（Yp0.2 ）、抗拉强度（TS ）、断 裂伸长率（El ）、屈服伸长率（Yp-El ）。 表