影响转炉提钒钒收率的因素分析及对策 黄正华 郭奠荣 （提钒炼钢厂，攀枝花 617023 ） 1 摘 要 为提高转炉提钒钒收率，最大限度地利用钒资源，本文对影响转炉提钒钒收率的因素进行了分析。分析认 为，影响钒收率的主要因素有半钢余钒高、组罐过程钒氧化、脱硫过程钒损失及出半钢过程钒渣流失等，并提出了 提高转炉提钒钒收率的措施。 关键词 转炉提钒 钒收率 铁水预处理 Analysis of Influencing Factors for Vanadium Recovery from Hot Metal during BOF Process and Countermeasures Huang Zhenghua Guo Dianrong (Vanadium Recovery and Steelmaking Plant of PZHsteel,Panzhihua, 617023) Abstract In order to increasing the yielding rate of vanadium from hot metal, and furthest utilization of vanadium resource, influencing factors of vanadium recovery from hot metal during BOF process are analyzed. The result showed that the influencing factors are the content of V in semi-steel, vanadium oxidization during hot metal ladle grouping, vanadium loss through desulfurization and vanadium slag loss through tapping. Last, the countermeasures for improving the yielding rate of vanadium are proposed. Key words extracting vanadium from Hot Metal during BOF Process, yielding rate of vanadium, hot metal pretreatment 1 引言 钒是重要的战略资源，我国蕴藏着极为丰富的钒钛磁铁矿资源，是世界生产钒及其相关产品的基地之一。 目前攀钢全流程（包括炼铁、炼钢、钒制品）的钒收率不足 50%，造成资源的极大浪费，为此，提高钒收 率的研究极为重要。目前提钒转炉钒收率为 80%左右，本文主要是对影响钒收率的因素进行分析，并提出 提高转炉提钒钒收率的措施。 2 影响转炉提钒钒收率因素 2.1 攀钢炼钢厂脱硫提钒工艺流程 攀钢炼钢厂脱硫提钒工艺流程见图 1。 黄正华，副主任工程师，从事铁水脱硫和转炉提钒方面的工作，359777287@，电话 8-676 第八届（2011 ）中国钢铁年会论文集 脱硫 转炉 含钒 组 炼 转炉 脱硫 图 1 攀钢脱硫提钒工艺流程 由于脱硫装置的布置分散，导致攀钢提钒炼钢厂脱硫提钒工艺有两个工艺流程，一是组罐后先脱硫，再 提钒，该部分占 60%；二是组罐后先提钒，后脱硫，该部分占40% 。 2.2