锌花控制技术研究与实践.pdfVIP

锌花控制技术研究与实践 孙 力 刘大亮 周国平 河北钢铁集团唐钢冷轧薄板厂，唐山 063016) 摘 要 本文在简要介绍锌花形成过程及合金元素对锌花状态影响的基础上，通过对镀锌原料粗糙度、锌液温度、 带钢入锌锅温度、工艺段带钢速度、特别是锌液成分等工艺参数的合理控制和优化，在无小锌花装置的条件下，成 功实现一条生产线兼容生产大、中、小锌花状态的产品。另外，通过对移动风机工艺参数的优化，使锌花均匀性明 显提高。 关键词 锌花 Sb 含量 移动风机 镀锌 Research and Practice on Spangle Controlling Technologies Sun Li Liu Daliang Zhou Guoping (Cold Rolling Strip Plant, Tangsteel, Heibei Iron and Steel Group, Tangshan, 063016) Abstract In the present work, on the base of the introduction of spangle formation and the effect of alloy elements on spangle, through optimizing and controlling properly such parameters as galvanized material roughness, temperature of molten zinc, temperature of strip into the pot, the strip speed of the process section, especially zinc liquid compositions, a compatible production of ordinary or finishing large, medium, small spangle state products in the same production line was successful achieved without small spangle device,. In addition, by optimizing movable blower process parameters, the spangle uniformity was improved significantly. Key words minimum spangle, Sb content, movable blower, galvanizing 1 引言 随着热镀锌产品日益在建筑、轻工、家电以及汽车行业的广泛应用，人们对热镀锌板表面的锌花状态要 求越来越严格：民用、建筑等普通商用板，要求尺寸较大的锌花供货；而小锌花则常常作为彩色涂层板基材 使用，或者经过光整后作为需要进一步涂漆的各种容器、家电、电气设备外壳等[1] 。获得多种不同的表面锌 花状态通常需要在多条专业化的热镀锌线上实现，成本太高。目前，鲜有关于能够使一条生产线同时兼容生 产大、中、小锌花状态产品的锌花状态控制技术的报道。 通常镀锌产品可以分为：大锌花(直径大于8mm)、中等锌花(直径大于5mm、且小于或等于8mm)、小 锌花(直径大于 1mm、且小于或等于5mm)和零锌花(直径小于或等于 1mm)等级别。在稳定其他工艺参数的 前提下，大锌花和小锌花之间可以利用小锌花装置，对镀锌板在镀后冷却上升段进行水雾冷却（加大冷却速 度）或者喷射锌粉（增加形核中心点）进行大、小锌花切换；也可以通过锌液成分、镀锌原料粗糙度、锌液 温度、带钢入锌锅温度、工艺段带钢速度等工艺参数的合理控制和优化进行大小锌花的切换。 通过对镀锌原料粗糙度、锌液温度、带钢入锌锅温度、工艺段带钢速度、特别是锌液中Sb 含量的控制，对 锌花尺寸进行合理调节，在同一条生产