400mm特厚板坯连铸质量缺陷成因与控制措施.pdfVIP

400mm 特厚板坯连铸质量缺陷成因与控制措施 马瑞金 （秦皇岛首秦金属材料有限公司，秦皇岛 066000 ） 摘 要 本文简要介绍了首秦公司 3 号连铸机主要工艺技术参数及多项先进技术，分析了生产 400mm 特厚连铸 板坯发生的外弧角横裂纹、宽面皮下裂纹、侧裂纹、宽面纵裂和内裂纹等的内外部质量缺陷成因，并提出了合理 控制钢水成分、优化结晶器振动参数、合理控制不同断面对应的结晶器锥度、优化结晶器足辊的位置及预紧力、 选用合适的浸入式水口和结晶器保护渣和调整优化二冷比水量等措施，有效的控制铸坯内外部质量缺陷的发生。 关键词 特厚板坯连铸 质量缺陷 控制措施 400mm Especially Thick Slab Continuous Casting Quality Defect Causes and Control Measure Ma Ruijin (Shouqin Metal Material Co. , Ltd. , Qinhuangdao, 066000) Abstract This paper briefly introduces shouqin company 3 main technology parameters caster and many advanced production technology, analyzes the special thick 400mm Waihu Angle slab happened under the crack, wide crack, side face crack, wide face in longitudinal crack and the internal and external quality defects such as crack formation, and puts forward the reasonable control steel components, mould oscillation parameters optimization, the reasonable control different sections corresponding mould taper, optimizing mould the foot roller position and preloaded force, selecting proper immersion type shuikou and mould protection slag and adjust optimization measures than two cold water, effective control of billet internal and external quality defect occurrence. 1 Key words especially thick slab continuous casting , quality defects , control measures 秦皇岛首秦金属材料有限公司（以下简称首秦）3 号板坯连铸机由西门子奥钢联设计研发，该铸机是世 界上首台带液芯弯曲矫直的特厚板坯连铸机，其所生产的 400mm 特厚板坯是当前直弧型板坯连铸机所能生 产的最大厚度。铸机采用上装引锭杆方式，中包钢水容量 46t，本体共有 19 个扇形段，基弧半径 11m，冶 金长度 45m，产品规格（250 、300、350、400 ）×（1600～2400 ）mm ，工作拉速0.52～1.1m/min，设计年 产量 110 万吨。 首秦 3 号铸机于 2010 年 6 月29 日投产热试，浇注断面350mm 。2010 年 7 月 17 日开始试生产400mm 特厚板坯，截止到 2011 年 4 月，400mm 特厚板坯共生产 75 个浇次，累计 625 炉，钢水 6 万吨，板坯 2558