邯钢电镀锌产品表面缺陷分析.pdfVIP

邯钢电镀锌产品表面缺陷分析 闫 磊 韩 冬 鲁安平 张 姝 蒋建朋 （河北钢铁集团邯钢公司技术中心，邯郸 056015 ） 1 摘 要 邯钢电镀锌生产线自建成投产以来，出现较多表面缺陷的质量问题，主要为丝状斑、水印、氧化边、色差。 本文采用宏观、微观检验，扫描电镜观察分析等方法对缺陷进行分析，对各缺陷的现象、产生原理、处理措施及改 善后效果进行了详细描述，以期能对同类型企业的生产提供一定参考。 关键词 邯钢 电镀锌 表面缺陷 丝状斑 水印 The Analysis of Handan Steel Electro Galvanized’s Defecets Yan Lei Han Dong Lu Anping Zhang Shu Jiang Jianpeng (Technology Center，Handan Iron and Steel Company, Hebei Iron and Steel Group,Handan,056015) Abstract There are many surface defect, include filar spot、watermark 、oxidized edge color aberration since Handan stelliron Electro Galvanized line builded., Defects are analysied by macro and micro examination, scanning electron microscope. The phenomenon of the defects, resulting in principle, measures and improved treatment results were described in detail in order to produce the same types of businesses to provide a reference. Key words Handan steeliron ，electro galvanized ，surface defect，filar spot，watermark 1 引言 根据市场变化情况，邯郸钢铁公司决定调整企业产品结构，将原有的 2 号彩涂生产线改造为电镀锌生产 线，生产具有高附加值的优质电镀锌钢板。改造后可年生产电镀锌板 18 万吨，产品厚范围 0.25～1.5 mm， 宽度范围为 900～1300 mm。 邯钢为首次涉及电镀锌的生产，相关技术及生产经验较少，因此，电镀锌机组自投产以来，持续出现色 差、丝状斑、氧化边、水印等缺陷，产品表面质量较差，投放市场后，对邯钢产品的声誉造成不利影响。因 此，针对电镀锌产品的质量缺陷，邯钢成立电镀锌产品质量攻关小组，通过调整电镀工艺及基板原料的轧制、 退火等工艺，提高电镀锌产品的表面质量，以获得电镀锌产品生产的关键技术，为实际生产提供指导作用。 2 邯钢电镀锌产线及生产工艺流程介绍 2.1 生产线简介 电镀锌产品由于其美观大方的表面和良好的耐腐蚀性能，被广泛应用于家用电器的生产。邯钢电镀锌生 产现采用无氰连续电镀生产工艺，生产线设计使用了较多独创技术，采用新型电镀槽，大大增加排气能力， 闫磊，男，硕士，工程师，从事新产品开发 yanlei@mail.hgjt.cn 第八届（2011 ）中国钢铁年会论文集 保证镀层表面质量；同时采用新型电解清洗槽，清洗效果良好。该产线主要单体设备由入口焊机、碱洗、酸 洗、电解清洗、电镀槽等单体设备组成，同时具有多种后处理设备，能提供磷化、耐指纹、钝化、涂油多种 后处理方式，产品种类丰富，能较好不同客户的需求。目前公司生产的耐指纹电镀锌板已被多家知名电器企 业使用。 2.2 生产工艺流程 上 料 上 卷 开 卷 剪 切 焊 接 挖 边