钢包顶渣改质剂冶金性能的研究.pdfVIP

钢包顶渣改质剂冶金性能的研究 廖 鹏 （新余钢铁集团有限公司，新余） 摘 要 本文从物理性能、顶渣改质后的成分变化、渣指数、硫容量和吸收夹杂物的性能等方面研究了钢包顶渣改 质剂的综合冶金性能。使用改质剂后顶渣转白较快，低碳、低硅钢经吹氩站处理后直上连铸，钢水流动性好，未发 生水口堵塞现象； 烟尘不大，能满足出钢和环保要求；钢水去硫效果好，脱硫率达到 40% 。最后根据研究结果， 提出了改质处理后钢包顶渣的最佳成分范围。1 关键词 顶渣改质剂 夹杂物 硫容量 水口堵塞 Research on Metallurgical Properties of Top Slag Modifier Liao Peng (Xinyu Iron Steel Group Co., Ltd., Xinyu) Abstract Metallurgical properties of top slag modifier was studied by means of physical properties, component changes after modifying, slag index, sulphur capacity and inclusion absorption etc. After slag modified, the following advantages could be obtained. Firstly, slag can be deoxided quickly, and low carbon silicon steel wouldnt occur nozzle clogging during continuous casting, which means molten steel has better cleanliness；Secondly, the modifying process has a little smoke; Thirdly, the process has better desulfurization, rate of desulfurization can be about 40%. Finally, according to study result, the best composition scope was proposed after top slag being modified. Key words top slag modifier, inclusion, sulphur capacity, nozzle clogging 为有效降低钢包顶渣的氧性，降低生产成本，减少连铸过程中水口堵塞现象，对生产过程所使用的钢包 顶渣改质剂进行了研究和比较分析。所谓改质剂，就是依靠改质剂中的强脱氧剂 Al ，将钢包顶渣中氧化铁 还原，最终使渣中 FeO、MnO 含量之和小于 5%，因此评价改质剂需要结合具体的工艺，在特定生产工艺条 件下，根据改质剂和后续渣料形成的顶渣性能，来评价它的适应性才有意义。 1 改质剂的物理性能 （1）钢包顶渣改质剂的主要成分见表 1。 表 1 钢包顶渣改质剂的成分范围 Al/% Al O /% H O/% SiO /% CaO/% 粒度/mm 2 3 2 2 ≥30 10～30 1 10 20 5~35 对改质剂先进行 X 衍射分析物相，半定量得到金属与氧化铝含量，然后 X 荧光分析其他成分含量，改 质剂 X 衍射半定量分析谱线见图 1。 廖鹏，男，博士，高级工程师，从事炼钢管理，lgcmanager@